Abstract:The effects of Li2O-B2O3-SiO2 (LBS) glass addition on densification and dielectric properties of (Ca1−xSrx)(Zr1−yMny)O3 fired in a reducing atmosphere have been investigated. The dielectric properties of (Ca1−xSrx)ZrO3 become better with decreasing the ratio of Sr/Ca. Substituting Zr by 0.2mol Mn, the dielectric loss of (Ca0.9Sr0.1)ZrO3 is greatly reduced, resulting in a Q × fr value of 30500GHz. To reduce the densification temperatures of (Ca0.9Sr0.1)(Zr0.8Mn0.2)O3 (CSZM9182) to the range cofirable with Cu electrode, 5–10vol% LBS glass is added and the densification temperature is lowered from 1500°C to 1030°C. The densification is further enhanced with increasing [B2O3]/[SiO2] ratio in the LBS glass, however, the dielectric properties are deteriorated. The above result is attributed to a chemical reaction taking place at the interface of CSZM9182-LBS during firing, which becomes more extensive with increasing [B2O3]/[SiO2] ratio in the LBS glass and tends to form a second phase of CaZr4O9. For the LBS glass with 40mol% Li2O, 20–50mol% B2O3, and 10–40mol% SiO2, the resulting CSZM9182 +5–10vol% LBS microwave ceramics have a dielectric constant of 23–27, Q × fr value of 2500–22,000GHz at 7.6–7.8GHz, and a temperature coefficient of resonant frequency (τf) of −22~ −7ppm/°C in the temperature range between 25°C and 80°C.

Low-fire Processing of Microwave BaTi4O9 Dielectric with BaO–Li2O–B2O3–SiO2–ZnO Glass

Low‐Fire Processing of Microwave BNBT‐Based High‐k Dielectric with Li2O–ZnO–B2O3 Glass

Low-Fire Processing of Microwave BNBT-Based High-k Dielectric with Li<sub>2</sub> O-ZnO-B<sub>2</sub> O<sub>3</sub> Glass

Low-fire processing of microwave BaTi4O9 dielectric with crystalline CuB2O4 and BaCuB2O5 additives

Low-Firing Ba_4(Nd_(0.85)Bi_(0.15))_(28/3)Ti_(18)O_(54) Microwave Ceramics

Low-Temperature Sintering and Microwave Dielectric Properties of Ba2Ti9O20 Ceramics with CaO–B2O3–ZnO Glass Additions

Low-Firing and Microwave Dielectric Properties of Ba2Ti9O20 with BaO–B2O3–ZnO Glass Addition

Low Firing and Microwave Dielectric Properties of BaTi4O9 with B2O3–ZnO–La2O3 Glass Addition

Low Temperature Sintering and Microwave Dielectric Properties of Ba4nd9.33ti18o54 Ceramics Doped with Crystallizable Glass

Low Temperature Sintering and Microwave Dielectric Properties of Ba<sub>4</sub>Nd<sub>9.33</sub>Ti<sub>18</sub>O<sub>54</sub> Ceramics Doped with Crystallizable Glass

Low-temperature firing and microwave dielectric properties of Ba–Nd–Ti with composite doping Li–B–Si and Ba–Zn–B glasses

Study on Low Temperature Sintering Behavior and Dielectric Properties of BaTi4O9/La2O3-B2O3-CaO Microwave Dielectric Ceramic

Low-fire Processing of Microwave (ca 1−x Sr X )(zr 1−y Mn Y )O 3 Dielectric with Li 2 O-B 2 O 3 -Sio 2 Glass in H 2 /N 2

Low temperature sintering BBSZ glass modified Li 2 MgTi 3 O 8 microwave dielectric ceramics

Microwave Dielectric Properties of BaO–4.3TiO2–0.5ZnO Ceramics with BaCu(B2O5)

Synthesis of Ba{[(Mg0.8Zn0.2)(0.98)Y-0.02](1/3)Tan(2/3)}O-3 Microwave Dielectric Ceramics with La2O3-B2O3-ZnO Glass for LTCC Application

Low-Fire Processing of Voltage-Tunable Ba0.6sr0.4tio3 Dielectric

Low-temperature Sintering and Microwave Dielectric Properties of BaO–0.15ZnO–4TiO 2 Ceramics with Li 2 O–B 2 O 3 –sio 2 Addition

Influence of Li2O–B2O3–SiO2 Glass on the Sintering Behavior and Microwave Dielectric Properties of BaO–0.15ZnO–4TiO2 Ceramics

Novel Thermal-Stable Low Temperature Sintered Ba 2 LiMg 2 V 3 O 12 Microwave Dielectric Ceramics with ZnO-P 2 O 5 -Mno 2 Glass Addition

Low-Temperature Firing and Microwave Dielectric Properties of Ca[(Li13Nb23)0.8Ti0.2]O3Ceramics with ZnB2O4Glass Addition