Low-temperature sintering kinetics and dielectric properties of Ba5Nb4O15 with B2O3–SiO2 glass
Xing Zhou,Chengli Sun,Dawei Xia,Lei Cao,Zhihong Wen,Shuren Zhang,Bin Tang
DOI: https://doi.org/10.1007/s10854-021-05542-0
2021-03-25
Abstract:For the first time, B<sub>2</sub>O<sub>3</sub>–SiO<sub>2</sub> (BS) glass-doped Ba<sub>5</sub>Nb<sub>4</sub>O<sub>15</sub> (BN) ceramics for low-temperature co-fired ceramic (LTCC) applications were facilely synthesized by the conventional solid-phase synthesis strategy. The influences of glass additive content on phase evolution, microstructure, and sintering activation energy were systematically deciphered associated with the microwave dielectric properties of the ceramics. While remaining original phase of Ba<sub>5</sub>Nb<sub>4</sub>O<sub>15</sub>, trace BS additive doping will effectively lessen the sintering temperature from 1350 to 925 °C excluding sacrificing microwave dielectric properties significantly. Optimized dielectric property is achieved via further time modulation: with 0.6 wt.% doping BS glass, Ba<sub>5</sub>Nb<sub>4</sub>O<sub>15</sub> ceramics sintered at 925 °C for 4 h exhibits best characteristics of <i>ε</i><sub><i>r</i></sub> = 41.2, <i>Q</i> × <i>f</i> = 22,238 GHz, <i>τ</i><sub><i>f</i></sub> = 53.1 ppm/°C. Therefore, Ba<sub>5</sub>Nb<sub>4</sub>O<sub>15</sub> ceramics doped with BS glass are potential candidates for LTCC.
engineering, electrical & electronic,materials science, multidisciplinary,physics, condensed matter, applied