Low‐Fire Processing of Microwave BNBT‐Based High‐k Dielectric with Li2O–ZnO–B2O3 Glass

yiting shih,jauho jean

DOI: https://doi.org/10.1111/jace.12602

IF: 4.186

2013-01-01

Journal of the American Ceramic Society

Abstract:The effects of Li2O-ZnO-B2O3 (LZB) glass addition on densification and dielectric properties of Ba-4(Nd0.85Bi0.15)(9.33)Ti18O54 (BNBT) have been investigated. At a given ratio of ZnO/B2O3, the glass softening point decreases, but the thermal expansion coefficient and dielectric constant increase with increasing Li2O content in the LZB glass. With 10vol% LZB glass, the densification temperature reduces greatly from 1300 degrees C for pure BNBT to 875 degrees C-900 degrees C for BNBT+LZB dielectric, and the densification enhancement becomes more significant with increasing Li2O content in the LZB glass. The above result is attributed to a chemical reaction taking place at the interface of LZB/BNBT during firing, which becomes less extensive with increasing Li2O content in the LZB glass. Therefore, more residual LZB glass, which acts as a densification promoter to BNBT, is left with increasing Li2O content. For the LZB glass with a Li2O content in the range 10-30mol%, the resulting 90vol% BNBT+10vol% LZB microwave dielectric has a dielectric constant of 55-70, product (Qxf(r)) of quality factor (Q) and resonant frequency (f(r)) of 1000-3000GHz at 5-5.79GHz, and a temperature coefficient of resonant frequency ((f)) of 10-60ppm/degrees C in the temperature range between 25 degrees C and 80 degrees C.