Abstract:The effects of Li2O-B2O3-SiO2 (LBS) glass addition on densification and dielectric properties of (Ca1−xSrx)(Zr1−yMny)O3 fired in a reducing atmosphere have been investigated. The dielectric properties of (Ca1−xSrx)ZrO3 become better with decreasing the ratio of Sr/Ca. Substituting Zr by 0.2mol Mn, the dielectric loss of (Ca0.9Sr0.1)ZrO3 is greatly reduced, resulting in a Q × fr value of 30500GHz. To reduce the densification temperatures of (Ca0.9Sr0.1)(Zr0.8Mn0.2)O3 (CSZM9182) to the range cofirable with Cu electrode, 5–10vol% LBS glass is added and the densification temperature is lowered from 1500°C to 1030°C. The densification is further enhanced with increasing [B2O3]/[SiO2] ratio in the LBS glass, however, the dielectric properties are deteriorated. The above result is attributed to a chemical reaction taking place at the interface of CSZM9182-LBS during firing, which becomes more extensive with increasing [B2O3]/[SiO2] ratio in the LBS glass and tends to form a second phase of CaZr4O9. For the LBS glass with 40mol% Li2O, 20–50mol% B2O3, and 10–40mol% SiO2, the resulting CSZM9182 +5–10vol% LBS microwave ceramics have a dielectric constant of 23–27, Q × fr value of 2500–22,000GHz at 7.6–7.8GHz, and a temperature coefficient of resonant frequency (τf) of −22~ −7ppm/°C in the temperature range between 25°C and 80°C.

Processing and Properties of a Low-Fire, High-K Dielectric in H 2 /N 2

Low‐Fire Processing of Microwave BNBT‐Based High‐k Dielectric with Li2O–ZnO–B2O3 Glass

Low-Fire Processing of Microwave BNBT-Based High-k Dielectric with Li<sub>2</sub> O-ZnO-B<sub>2</sub> O<sub>3</sub> Glass

Low-fire Processing of Microwave (ca 1−x Sr X )(zr 1−y Mn Y )O 3 Dielectric with Li 2 O-B 2 O 3 -Sio 2 Glass in H 2 /N 2

High-Q Microwave Dielectric Properties Of Li(Zn0.95co0.05)(1.5)Sio4 Ceramics For Ltcc Applications

Low-Fire Processing And Properties Of Ferrite Plus Dielectric Ceramic Composite

Experiment and calculation: The Li(Zn, Mn)PO<sub>4</sub> solid solution ceramics with low dielectric constant, high quality factor, and low densification temperature

Low-Temperature Firing and Microwave Dielectric Properties of Ca[(Li13Nb23)0.8Ti0.2]O3Ceramics with ZnB2O4Glass Addition

Low-fire processing of microwave BaTi4O9 dielectric with crystalline CuB2O4 and BaCuB2O5 additives

Room temperature giant dielectric behavior of BaTiO3/Ni0.5Zn0.5Fe2O4 composite ceramic

Bond Characteristics And Microwave Dielectric Properties Of High-Q Materials In Li-Doped Zn3b2o6 Systems

Low-fire Processing of Microwave BaTi4O9 Dielectric with BaO–Li2O–B2O3–SiO2–ZnO Glass

Effect of ZnO and B2O3 on the Sintering Temperature and Microwave Dielectric Properties of LiNb0.6Ti0.5O3 Ceramics

Low-firing, Temperature Stable and Improved Microwave Dielectric Properties of ZnO TiO2Nb2O5 Composite Ceramics

Low Firing and Microwave Dielectric Properties of BaTi4O9 with B2O3–ZnO–La2O3 Glass Addition

Low Dielectric Permittivity and Low Loss of Low Temperature Co-Fired Li 2 Zn X Mg 0.98−x Co 0.02 SiO 4 Ceramics with LiF–Bi 2 O 3 Additives

Low Sintering of the Temperature-Stable Dielectric Ceramics Based on Barium Titanate in Reducing Atmosphere

The effect of composition on Li2(Mg0.3Zn 0.7)Ti3O8-xTiO2 microwave dielectric ceramics for low temperature co-fired ceramics technology application

A Synergistic Effect of Li-B-Si Glass and La-B on Low-Temperature Sintering of Bao-0.15zno-4tio(2) Dielectric Ceramic

Silver Co-Firable Zntinb2o8 Microwave Dielectric Ceramics With Li2o-Zno-B2o3 Glass Additive

Sintering Behavior and Microwave Dielectric Properties of LMZBS Glass Doped Li 3 Mg 4 NbO 8 Ceramics for LTCC Applications