Microwave Dielectric Properties of TiO 2 -Added Li 2 ZnTi 3 O 8 Ceramics Doped with Li 2 O-Al 2 O 3 -B 2 O 3 Glass
Ying-xiang Li,Zhen-jun Qin,Bin Tang,Shu-ren Zhang,Geng Chang,Hao Li,He-tuo Chen,Han Yang,Jun-shan Li
DOI: https://doi.org/10.1007/s11664-014-3433-6
IF: 2.1
2015-01-01
Journal of Electronic Materials
Abstract:The effect of Li2O-Al2O3-B2O3 (LAB) glass addition on phase composition, microstructure and the microwave dielectric properties of Li2ZnTi3O8 ceramics with TiO2 were investigated using x-ray diffraction (XRD), scanning electron microscopy (SEM), energy-dispersive x-ray spectroscopy (EDS) and a vector network analyzer. With the addition of 17 mol% TiO2 on Li2ZnTi3O8 ceramics, the temperature coefficient of the resonant frequency (τ ƒ) value could be adjusted to +3.3 ppm/°C. When a small amount of LAB glass was added to the Li2ZnTi3O8 + 17 mol% TiO2 materials, the sintering temperature could be significantly lowered from 1160°C to 900°C. With increasing the LAB glass, the Q × f value first increased and then decreased. Typically, the 1 wt.% LAB glass-added Li2ZnTi3O8 + 17 mol% TiO2 ceramics sintered at 900°C for 4 h had good microwave dielectric properties with εr = 26.8, Q × f = 28,000 GHz and τ ƒ = + 2.5 ppm/°C, which made it a promising ceramic for LTCC technology application.