Effects of La2O3–B2O3 on the flexural strength and microwave dielectric properties of low temperature co-fired CaO–B2O3–SiO2 glass–ceramic

Xiaohua Zhou,Enzhu Li,Shilin Yang,Bo Li,Bin Tang,Ying Yuan,Shuren Zhang

DOI: https://doi.org/10.1016/j.ceramint.2012.03.072

IF: 5.532

2012-09-01

Ceramics International

Abstract:The La2O3–B2O3 (LB) addition, synthesized using the traditional solid-state reaction process, was chosen as a novel sintering aid of the low temperature co-fired CaO–B2O3–SiO2 (CBS) glass–ceramic. The effects of LB on the flexural strength and microwave dielectric properties have been investigated. The LB addition promotes the crystallization of the CaSiO3 but high amount of the LB addition leads to the formation of more pores. The CBS sample with 4wt% LB addition sintered at 850°C for 15min shows good properties: flexural strength=193MPa, ɛr=6.26 and loss=9.96×10−4 (10GHz).

materials science, ceramics