Abstract:CaO–B2O3–SiO2 (CBS) glass–ceramics were used as the main research object in this study. Based on the predecessors' work, we optimized the ternary components of glass–ceramics to observe its effects on the structure, sintering performance and dielectric properties of glass–ceramics. When the content of B2O3 was 15.5 mol%, the Ca/Si ratio was 0.61–0.62, the glass–ceramics were transparent after water quenching, and it could achieve sintering densification under 850 °C. When the Ca/Si ratio was < 0.61 and > 0.62, the state of glass–ceramics was changed from transparent to milk-whited. As for sintering, when the sintering temperature was above 900 °C, they could achieve sintering densification. On the basis of it, we fixed the Ca/Si ratio of 0.61, and adjusted the content of B2O3. We found that with the increasing of the B2O3 content, the transparency of glass–ceramics was worse and worse, and when the samples obtained the highest density, the sintering temperature were elevated from 820 to 920 °C. According to the XRD analysis, with the B2O3 content added, the CaB2O4 crystal phases in the glass–ceramics was increased, so the permittivity of the glass–ceramics was increased. When the Ca/Si ratio was 0.61 and the B2O3 content was 15.5 mol%, the sintered density of CBS glass–ceramics was 2.42 g/cm3 at 850 °C, the permittivity and dielectric loss was εr = 5.88, tanδ = 2.8 × 10−3 at 10 kHz.

Densification Behavior and Dielectric Properties of CaO-B2O3-SiO2 System Glass-Ceramics Containing ZrO2

Crystallization, sinterability and dielectric properties of CaO–B 2 O 3 –SiO 2 glass ceramics with Al 2 O 3 additives

Effects of B2O3 content on crystallization behavior and properties of low temperature co-fired CaO-B2O3-SiO2 glass-ceramics

Sintering,crystallization and Dielectric Properties of CaO-B 2 O 3 -Sio 2 System Glass Ceramics

Microstructure and crystallization properties of Na2O-CaO-SiO2 glass system with different ZrO2 content

Crystallization mechanism and properties of CaO-B2O3-SiO2-Nb2O5 (CBSN) glass-ceramics

Microstructure and microwave dielectric properties of CaO-B2O3-SiO2 glass ceramics with various B2O3 contents

Characterizations of CaO–B2O3–SiO2 glass–ceramics: Thermal and electrical properties

Study on properties of CaO-B 2O 3-SiO 2 glass ceramics contained alkali ions

The effects of Ca/Si ratio and B2O3 content on the dielectric properties of the CaO–B2O3–SiO2 glass–ceramics

Network structure, crystallization behavior, and microwave dielectric properties of ZnO-B2O3 glass-ceramics with ZrO2 additions

Sintering behaviors, microstructures and dielectric properties of CaO-B2O3-SiO2 glass ceramic for LTCC application with various network modifiers content

Crystallization, structure, and properties of TiO2-ZrO2 co-doped MgO-B2O3-Al2O3-SiO2 glass-ceramics

Densification and Dielectric Properties of CaO–B2O3–SiO2 System Glass Ceramics

Effect of Ca/Si ratio on the microstructures and properties of CaO–B2O3–SiO2 glass-ceramics

Effects of La2O3–B2O3 on the flexural strength and microwave dielectric properties of low temperature co-fired CaO–B2O3–SiO2 glass–ceramic

Low-fire Processing of Microwave (ca 1−x Sr X )(zr 1−y Mn Y )O 3 Dielectric with Li 2 O-B 2 O 3 -Sio 2 Glass in H 2 /N 2

Low-Temperature Sintering and Microwave Dielectric Properties of Ba2Ti9O20 Ceramics with CaO–B2O3–ZnO Glass Additions

Densification and microwave dielectric properties of CaO–B2O3–SiO2 system glass–ceramics

Effects of MgO/CaO ratio on the crystal phase composition and performance of MgO-CaO-B2O3-SiO2 glass–ceramics for LTCC applications

Effect of SiO2/BaO ratio on sintering behavior, crystallization behavior, and properties of SrO–BaO–B2O3–SiO2 glass-ceramics