Low-temperature Sintering of (co0.35zn0.65)tinb2o8 Temperature-Stable Microwave Dielectric Ceramics with BaCu(B2O5) Additions
Jia-Pei Jiang,Chang-Hao Wang,Wei Wang,Zhong-Qi Shi,Xiao-Gang Yao,Hui-Xing Lin,Tao Zhou,Ya-Wei Chen,Qi-Xin Liang,Mei-Rong Zhang,Di Zhou
DOI: https://doi.org/10.1016/j.jeurceramsoc.2024.04.034
IF: 5.7
2024-01-01
Journal of the European Ceramic Society
Abstract:In this study, the effects of BaCu(B2O5) (BCB) additive on the low-temperature sintering behaviour, microstructure evolution and microwave dielectric properties of (Co0.35Zn0.65)TiNb2O8 (CZTN) ceramics were systematically investigated by introducing the additive into the solid-state sintering process. Adding BCB successfully lowered CZTN ceramics' sintering temp from 1150 degrees C to 925 degrees C while preserving their superior microwave dielectric properties at the lower temperature. However, excessive BCB tends to disrupt the equilibrium between the native ixiolite and rutile phases within the ceramic matrix, thereby instigating a relative augmentation of the rutile phase, ultimately culminating in a positive shift in the temperature coefficient of the resonant frequency. Specific experimental data show that the CZTN ceramics prepared with a BCB content of 4 wt% exhibited good microwave dielectric properties after sintering at 925 degree celsius for 4 h: relative dielectric constant (epsilon r) = 36.7, quality factor (Q x f) = 19,880 GHz, and tau f = +14.2 ppm/degree celsius. In addition, the ceramic system showed good chemical compatibility when co-fired with Ag without significant elemental diffusion. This work reveals the specific role of BCB in enhancing low-temperature sintering of CZTN ceramics and pinpoints its ideal addition range, thereby offering crucial scientific insights and technical support for developing high-performance microwave dielectric ceramics for LTCC technology.