Abstract:A new low-temperature microwave dielectric ceramic with low-permittivity was found and investigated in the CaO–MgO–SiO2–TiO2 system. Phase constitutes and dielectric properties of (Ca1−x,Mgx)SiO3 (x=0.1–0.5) ceramics were studied with different x contents, and CaTiO3 demonstrated an effective compensation in (Ca1−x,Mgx)SiO3 τf value. The 0.88CaMgSi2O6–0.12CaTiO3 compositions show a relatively low-permittivity (∼9.42), high Q×f values up to 52,800GHz, and near-zero temperature coefficients (5.6ppm/°C), which were obtained via sintering at 1300°C. The addition of ≤2.0wt% Li2CO3–V2O5 was very effective in lowering the sintering temperature (Ts), and dense ceramics could be obtained at Ts≤900°C. The addition of Li2CO3–V2O5 does not induce apparent degradation in the microwave properties. The specimens with 1wt% Li2CO3–V2O5 sintered at 880°C for 2h shows excellent dielectric properties: ɛr=9.23, Q×f=46,200GHz, and τf=1.3ppm/°C. The low-temperature sintering ceramics powders were suitable for the tape casting process. Also, the material is compatible with Ag electrodes, and therefore, is suitable for LTCC application.

Low Temperature Sinter-Ability of Microwave Dielectric Ceramics 0.4(Ca<sub>0.61</sub>Nd<sub>0.26</sub>)TiO<sub>3</sub>-0.6(Li<sub>0.5</sub>Sm<sub>0.5</sub>)TiO<sub>3</sub>

Low temperature sinter-ability of microwave dielectric ceramics 0.4(Ca 0.61Nd0.26)TiO3-0.6(Li0.5Sm 0.5)TiO3

Low-Temperature Firing And Microwave Dielectric Properties Of Ca[(Li0.33nb0.67)(0.9)Ti-0.1]O3-Delta Ceramics With Lif Addition

Temperature Compensated (1-x)(Na<sub>0.5</sub>La<sub>0.5</sub>)TiO<sub>3</sub>+xCeO<sub>2</sub> Microwave Dielectric Ceramics Incorporated with Copper Oxide

Low-Firing Ba_4(Nd_(0.85)Bi_(0.15))_(28/3)Ti_(18)O_(54) Microwave Ceramics

Effects Of Catio(3)On Microstructures And Properties Of (1-X) Znal2o4-Xmg(2) Tio4 (X=0.1) Microwave Dielectric Ceramics

Low-temperature sintering and dielectric properties of high-permittivity microwave (Ca, Nd)TiO 3 ceramics

Low -temperature sintering of Al2O3 microwave dielectric ceramic doped with CuO-TiO2 gel

Low-temperature sintering and phase component modulation of 0.95MgTiO3–0.05CaTiO3 microwave dielectric ceramics

Low-temperature Sintering and Microwave Dielectric Properties of ZnTiO3-based LTCC Materials

Microwave dielectric properties of Na2O–Ln2O3–MoO3–TiO2 (Ln = Nd, La and Ce) system with low‐sintering temperature

Low-Temperature Sintering and Processing of Microwave Dielectric aBaO plus bNb(2)O(5) Ceramics

High dielectric constant perovskite ceramic sintered at low temperature with La–Li–Zn–B glass for LTCC applications

Simultaneously achieving high permittivity and low loss in CuO/Nb2O5 substituted Li2O-TiO2-Nb2O5 low-temperature microwave dielectric ceramics

Low-Temperature Firing and Microwave Dielectric Properties of Ca[(Li1/3nb2/3)(0.84)Ti-0.16]O3-Delta Ceramics for Ltcc Applications

Low Temperature Sintering and Microwave Dielectric Properties of Zr 0.3 (zn 1/3 Nb 2/3 ) 0.7 TiO 4 Ceramics Doped with CuO-B 2 O 3

Median Temperature Sintered Ca[(Li1/3Nb2/3)0.8Ti0.2]O3-σMicrowave Ceramics

A New Microwave Ceramic with Low-Permittivity for Ltcc Applications

Modification of Low Temperature Sintered CMS Microwave Dielectric Ceramics Doped with Nanopowder

Low Temperature Sintering of Li 2 (mg 0.3 Zn 0.7 )ti 3 O 8 -0.12Tio 2 Microwave Dielectric Ceramics with Controllable Grain Size

Low Temperature Sinter-Ability of Microwave Dielectric Ceramics 0.4(Ca&lt;sub&gt;0.61&lt;/sub&gt;Nd&lt;sub&gt;0.26&lt;/sub&gt;)TiO&lt;sub&gt;3&lt;/sub&gt;-0.6(Li&lt;sub&gt;0.5&lt;/sub&gt;Sm&lt;sub&gt;0.5&lt;/sub&gt;)TiO&lt;sub&gt;3&lt;/sub&gt;