Median Temperature Sintered Ca[(Li1/3Nb2/3)0.8Ti0.2]O3-σMicrowave Ceramics

ZHANG Qi-Long,YANG Hui,TONG Jian-xi

DOI: https://doi.org/10.3969/j.issn.1001-2028.2005.05.011

2005-01-01

Abstract:The effects of Bi2O3 addition on the sinterability, crystal structure and dielectric properties of CLNT ceramics were investigated. The sintering temperature was decreased from 1 150℃ to 1 050℃ with 4 wt%~10 wt% Bi2O3 addition due to Bi2O3 and Bi2O3-TiO2 liquid phase sintering effect. X-ray diffractometry analyses results indicate that the phase divide and produce the second phase.When mass fraction of Bi2O3 is less than 4wt%,the dielectric constant change a little. When mass fraction of Bi2O3 is more than 4wt%,the dielectric constant decreases due to pore .The Q·f value decrease owing to Bi2O3-TiO2 phase formation and the τf values are shifted toward negative direction with the increase of Bi2O3 addtion.The er value of 37.8, Q·f value of 11 030 GHz and τf value of 12×10–6℃–1 are obtained for CLNT ceramics with 4 wt% Bi2O3 sintered at 1 050℃ for 4 h.