Effect of TiO 2 whiskers on the microstructure and mechanical and dielectric properties of MgO ceramics
Qi Yuan,Sen Wang,Wencai Hu,Tao Wang,Gaobin Liu,Xueyan Han,Feixiang Guo,Yongheng Fan
DOI: https://doi.org/10.1016/j.ceramint.2022.10.022
IF: 5.532
2022-12-22
Ceramics International
Abstract:Here, TiO 2 (w)-containing MgO ceramics were sintered at 1450 °C using a solid-phase method, and the effect of TiO 2 (w) addition on the sintering, dielectric, and mechanical properties of MgO ceramics was investigated. The results indicate that TiO 2 (w) reacts with MgO during sintering to form a new phase, Mg 2 TiO 4 , and a 'special' structure of Mg 2 TiO 4 surrounds the MgO grains. This structure contributes to the densification of the MgO ceramics during sintering, thereby improving the dielectric and mechanical properties. The dielectric constants of MgO ceramic samples with different TiO 2 (w) additions fluctuated between 10.6 and 11.9, and the loss tangent values fluctuated between 1.3 × 10 -4 and 4.0 × 10 –4 ; when TiO 2 (w) was added at 12 wt%, the relative density, flexural strength, fracture toughness, nanohardness, elastic modulus, and Vickers hardness of the sintered samples achieved a maximums of 97.4%, 221.0 MPa, 3.2 MPa m 1/2 , 4.2 GPa, 383.1 GPa, and 1048.7 HV, respectively. The introduction of TiO 2 (w) resulted in the formation of continuous and uniformly distributed intermediate phases inside the material, which improved the MgO ceramic densities, and dielectric and mechanical properties.
materials science, ceramics