Abstract:Microwave dielectric properties of low temperature sintering ZnNb 2 O 6 ceramics doped with CuO-V 2 O 5 -Bi 2 O 3 additions were investigated systematically. The co-doping of CuO, V 2 O 5 and Bi 2 O 3 can significantly lower the sintering temperature of ZnNb 2 O 6 ceramics from 1150 to 870 ∘ C. The secondary phase containing Cu, V, Bi and Zn was observed at grain boundary junctions, and the amount of secondary phase increased with increasing CuO-V 2 O 5 -Bi 2 O 3 content. The dielectric properties at microwave frequencies (7–9 GHz) in this system exhibited a significant dependence on the relative density, content of additives and microstructure of the ceramics. The dielectric constant (ε r ) of ZnNb 2 O 6 ceramics increased from 21.95 to 24.18 with increasing CuO-V 2 O 5 -Bi 2 O 3 additions from 1.5 to 4.0 wt%. The quality factors ( Q × f ) of this system decreased with increasing CuO-V 2 O 5 -Bi 2 O 3 content and ranged from 36118 to 67100 GHz for sintered ceramics, furthermore, all Q × f values of samples with CuO-V 2 O 5 -Bi 2 O 3 additions are lower than that of un-doped ZnNb 2 O 6 ceramics sintered at 1150 ∘ C for 2 h. The temperature coefficient of resonant frequency (τ f ) changed from −33.16 to −25.96 ppm/ ∘ C with increasing CuO-V 2 O 5 -Bi 2 O 3 from 1.5 to 4.0 wt%

Effects of additives on microstructures and microwave dielectric properties of ZnNb2O6 ceramics

Effects of CuO-V<sub>2</sub>O<sub>5</sub>-Bi<sub>2</sub>O<sub>3</sub> Additions on the Microstructure and Microwave Dielectric Properties of 0.42ZnNb<sub>2</sub>O<sub>6</sub>-0.58TiO<sub>2</sub> Ceramics

Effects of CuO-V2O5-Bi2O3 Additions on the Microstructure and Microwave Dielectric Properties of 0.42Znnb2o6-0.58Tio2 Ceramics

Low-Temperature Firing and Microwave Dielectric Properties of Zn3nb2o8 Ceramics with Cuo-V2o5-Bi2o3

Microwave Dielectric Properties of CuO-V 2 O 5 -Bi 2 O 3 -Doped ZnNb 2 O 6 Ceramics with Low Sintering Temperature

Microwave Dielectric Properties of Cuo-V2o5-Bi2o3-Doped Znnb2o6 Ceramics with Low Sintering Temperature

Structure characteristics of low-temperature-sintered ZnNb 2O6 microwave dielectric ceramics

Structure characteristics of low-temperature-sintered ZnNb2O6 microwave dielectric ceramics

Low temperature sintered ZnNb2O6 microwave dielectric ceramics doped with CuO-Bi2O3-V2O5 additions

Low-temperature firing and microwave dielectric properties of ZnO–Nb2O5–TiO2–SnO2 ceramics with CuO–V2O5

Effects of ZnO–xV2O5 Substitution on the Microstructure and Microwave Dielectric Properties of ZnNb2O6 Ceramics

Microstructure and microwave dielectric properties of Zn(Nb 0.9v0.1)2O6 ceramics sintered at low temperatures

Effect of B2O3 Doping on Microwave Dielectric Properties of (Zn0.5Mg0.5)Nb2O6 Ceramics

Effects Of Catio(3)On Microstructures And Properties Of (1-X) Znal2o4-Xmg(2) Tio4 (X=0.1) Microwave Dielectric Ceramics

Effect of B_2O_3 Doping on Microwave Dielectric Properties of (Zn_(0.5)Mg_(0.5))Nb_2O_6 Ceramics

Microstructure and microwave dielectric properties of ZnO-B2O3 doped ceramics

Low-Firing Ba_4(Nd_(0.85)Bi_(0.15))_(28/3)Ti_(18)O_(54) Microwave Ceramics

Influence of CuO on Sintering Temperature and Microwave Dielectric Properties of (zn_(0.5)mg_(0.5))nb_2o_6 Ceramics

Low-Temperature Sintering and Microwave Dielectric Properties of Znzrnb2o8 Ceramics with Bacu(B2o5) Addition

Effect of ZnO-V2O5Co-doping on phase stability and microwave dielectric properties of ZnTiO3 ceramics

Low temperature sintering and microwave dielectric properties of BaO–0.6ZnO–2.9TiO 2 ceramics using BaCu(B 2 O 5 ) addition