Effects of ZnO–xV2O5 Substitution on the Microstructure and Microwave Dielectric Properties of ZnNb2O6 Ceramics

Jin Wang,Zhenxing Yue,Jing Yan,Zhilun Gui,Longtu Li

DOI: https://doi.org/10.1007/s10832-007-9093-7

2007-01-01

Journal of Electroceramics

Abstract:The ZnO–xV2O5 substituted ZnNb2O6 ceramics with chemical formula Zn(Nb0.9V x )2O5.5+5x (0 < x ≤ 0.10) were prepared by solid-state reaction route. The densities, microstructures and microwave dielectric properties were investigated according to the different substitution amount of V2O5 and sintering temperature. A small amount of substitution of ZnO–xV2O5 was effective to lower sintering temperature of ZnNb2O6 ceramics from 1,150 °C to 900 °C. The V2O5 substitution led to growth of rod-like grains with the help of liquid phase formed from ZnO and V2O5. The dielectric properties depended largely on the amount of V2O5 substitution and sintering temperature. The dense ceramics with x = 0.05 were obtained at 950 °C, which had excellent dielectric properties: ɛr = 24, Q × f = 72,800 GHz and τf = −63.5 ppm/°C. The interface analysis for cofired multilayer composites composed of the present LTCC and metal Ag demonstrated good co-firing chemical compatibility at co-sintering temperature.