Low-temperature sintered Zn(NbV)O microwave dielectric ceramics with high value for LTCC application

J WANG,Z YUE,Z GUI,L LI

DOI: https://doi.org/10.1016/j.jallcom.2004.07.086

IF: 6.2

2005-01-01

Journal of Alloys and Compounds

Abstract:V2O5-substituted ZnNb2O6 ceramics with composition of Zn(Nb1−xVx/2)2O6−2.5x (i.e. ZNV) were prepared by the solid-state reaction method. The substitution of V2O5 in ZnNb2O6 ceramics could effectively lower the sintering temperature to ∼950°C in comparison to 1150°C for pure ZnNb2O6 ceramics. The phase composition and microstructure of samples with different substitution amounts of V2O5 sintered at different temperatures were investigated systematically. The low-temperature sintering behaviors and good microwave dielectric properties, especially high Q×f values, indicate that ZNV ceramics could be a very promising candidate for low-temperature co-fired ceramic (LTCC). The samples with chemical formula Zn(Nb0.95V0.025)2O5.875 sintered at 1000°C exhibit the optimum properties: ɛr=23.8, Q×f=64,000GHz and τf=−50ppm/°C. The co-firing behavior with Ag electrodes has also been investigated.