Abstract:1. Excellent microwave dielectric properties with a low ԑr ∼6.52, a high Q × f ∼46 010 GHz and a TCF∼−14ppm∘C−1 were obtained in the 0.5BaCuSi4O10–0.5BaCuSi2O6 ceramic sintered at 1060°C. 2. The 0.5BaCuSi4O10–0.5BaCuSi2O6‐based ceramics have excellent temperature stability. 3. The 0.5BaCuSi4O10–0.5BaCuSi2O6 ceramics doped with LiF and LBSCA glass are suitable for LTCC technology due to their low sintering temperatures (from 830°C to 890°C) and good chemical compatibility with silver. In this work, the 0.5BaCuSi4O10–0.5BaCuSi2O6‐based ceramics were synthesized using a standard solid‐phase reaction process, and the inherent relationship between crystal structure and microwave dielectric properties was thoroughly explored. The crystal structure of the 0.5BaCuSi4O10–0.5BaCuSi2O6 ceramic was determined by X‐ray diffractometer, which confirmed the existence of two phases. Microstructure observation of the ceramics was obtained by scanning electron microscope (SEM). Excellent microwave dielectric properties with a low ԑr ∼6.52, a high Q × f ∼46 010 GHz, and the temperature coefficient of resonant frequency (TCF) ∼−14 ppm°C−1 were obtained in the 0.5BaCuSi4O10–0.5BaCuSi2O6 ceramic sintered at 1060°C. By adding sintering additives LiF and Li2O–B2O3–SiO2–CaO–Al2O3 (LBSCA) glass, the sintering temperature was decreased from 1060°C to 870°C. Good microwave dielectric properties with a ԑr ∼6.59, a Q × f ∼18 820 GHz, and TCF ∼−14 ppm°C−1 were achieved in the 0.5BaCuSi4O10–0.5BaCuSi2O6 ‐2 wt.% LiF, 1 wt.% LBSCA (2F1LBSCA) ceramic sintered at 870°C. The low‐temperature firing ceramics could also be well co‐fired with Ag with good chemical compatibility. These results indicated that the 0.5BaCuSi4O10–0.5BaCuSi2O6 ceramic with 2F1LBSCA additions can be utilized in low‐temperature co‐fired ceramics technology to produce high‐frequency communication components.

A new high-Q×f Li4NbO4F microwave dielectric ceramic for LTCC applications

Low-temperature Co-Fired Ceramics with High Thermal Expansion and Reliability for Millimeter-Wave Antennas

Low-Temperature Firing And Microwave Dielectric Properties Of Ca[(Li0.33nb0.67)(0.9)Ti-0.1]O3-Delta Ceramics With Lif Addition

A novel high-Q oxyfluoride Li4Mg2NbO6F microwave dielectric ceramic with low sintering temperature

Novel series of high-Q oxyfluoride microwave dielectric ceramics for LTCC applications

Li4Mg3Ti2O9: A novel low-loss microwave dielectric ceramic for LTCC applications

Temperature stable Li5.5Nb1.5O6F-based microwave dielectric ceramics for LTCC applications

Enhanced the temperature stability of low-fired Li3Mg2NbO6 microwave dielectric ceramics for LTCC application

Li5Ti2O6F: a new low-loss oxyfluoride microwave dielectric ceramic for LTCC applications

Low-fired Li3Mg2NbO6 microwave dielectric ceramics by adding LMBCS glass for LTCC application

A New Microwave Ceramic with Low-Permittivity for Ltcc Applications

Low temperature sintered Li6MgTiNb1-xVxO8F microwave dielectric ceramics with high-quality factor

Novel Low-Firing Forsterite-Based Microwave Dielectric for Ltcc Applications

Low-Firing Ba_4(Nd_(0.85)Bi_(0.15))_(28/3)Ti_(18)O_(54) Microwave Ceramics

Simultaneously achieving high permittivity and low loss in CuO/Nb2O5 substituted Li2O-TiO2-Nb2O5 low-temperature microwave dielectric ceramics

Microwave Dielectric Properties of Low-Fired Li2TiO3–MgO Ceramics for LTCC Applications

A low-sintering temperature microwave dielectric ceramic for 5G LTCC applications with ultralow loss

Novel ultra-low loss and low-fired Li8MgxTi3O9+xF2 microwave dielectric ceramics for resonator antenna applications

Microwave dielectric properties of Li2WO4-added SrWO4 ceramics for LTCC applications

Developing high performance, low temperature sintering and temperature stable K40 material in Co2O3/Nb2O5-modified Ba3Ti4Nb4O21 microwave dielectric ceramics for 5G-LTCC communication devices

Effect of LiF and LBSCA glass on the microwave dielectric properties of 0.5BaCuSi4O10–0.5BaCuSi2O6‐based ceramics for LTCC applications