A New Microwave Ceramic with Low-Permittivity for Ltcc Applications

Qi-Long Zhang,Hui Yang,Hui-Ping Sun

DOI: https://doi.org/10.1016/j.jeurceramsoc.2007.07.003

IF: 5.7

2008-01-01

Journal of the European Ceramic Society

Abstract:A new low-temperature microwave dielectric ceramic with low-permittivity was found and investigated in the CaO–MgO–SiO2–TiO2 system. Phase constitutes and dielectric properties of (Ca1−x,Mgx)SiO3 (x=0.1–0.5) ceramics were studied with different x contents, and CaTiO3 demonstrated an effective compensation in (Ca1−x,Mgx)SiO3 τf value. The 0.88CaMgSi2O6–0.12CaTiO3 compositions show a relatively low-permittivity (∼9.42), high Q×f values up to 52,800GHz, and near-zero temperature coefficients (5.6ppm/°C), which were obtained via sintering at 1300°C. The addition of ≤2.0wt% Li2CO3–V2O5 was very effective in lowering the sintering temperature (Ts), and dense ceramics could be obtained at Ts≤900°C. The addition of Li2CO3–V2O5 does not induce apparent degradation in the microwave properties. The specimens with 1wt% Li2CO3–V2O5 sintered at 880°C for 2h shows excellent dielectric properties: ɛr=9.23, Q×f=46,200GHz, and τf=1.3ppm/°C. The low-temperature sintering ceramics powders were suitable for the tape casting process. Also, the material is compatible with Ag electrodes, and therefore, is suitable for LTCC application.