Sintering behavior and microwave dielectric properties of Sr2CeO4 ceramics doped with Li2CO3-Bi2O3
Fuming Zhou,Hao Wang,Jianming Guo,Hui Yang,LingFeng Li,Qilong Zhang
DOI: https://doi.org/10.1007/s10854-020-04682-z
2020-10-23
Abstract:Microwave dielectric ceramics Sr<sub>2</sub>CeO<sub>4</sub> + <i>n</i> wt% Li<sub>2</sub>CO<sub>3</sub>—Bi<sub>2</sub>O<sub>3</sub> (LB) (1 ≤ <i>n</i> ≤ 4, L: B = <i>x</i>: <i>y</i>, weight ratio) were prepared by a traditional solid-state reaction method. The effects of LB additives on the phase formation, microstructure, sintering behavior, and microwave dielectric properties of Sr<sub>2</sub>CeO<sub>4</sub> ceramics were investigated. The sintering temperature can be reduced obviously from 1270 to 950 °C because of the liquid phase formation of LB. Single-phase Sr<sub>2</sub>CeO<sub>4</sub> ceramics with dense structure and homogenous grains were obtained by adding 1wt% LB. With LB content increasing, Q × f values would decrease because secondary-phase SrCeO<sub>3</sub> appeared in the ceramics. When the content of LB was fixed at 1 wt%, the sintering temperature and Q × f value would decrease simultaneously with the ratio of Li<sub>2</sub>CO<sub>3</sub> increasing. Desirable performances of Sr<sub>2</sub>CeO<sub>4</sub> + 1wt% LB ceramics: (<i>ε</i><sub><i>r</i></sub> = 14.36, Q × f = 102,023 GHz and <i>τ</i><sub><i>f</i></sub> = − 66.42 ppm/°C, L:B = 2:8) and (<i>ε</i><sub><i>r</i></sub> = 13.56, Q × f = 70,109 GHz, τ<sub>f</sub> = − 64.17 ppm/°C, L:B = 8:2) can be achieved at 1075 °C and 950 °C, respectively, suggesting that Sr<sub>2</sub>CeO<sub>4</sub>–LB ceramics have a great potential for millimeter-wave applications.
engineering, electrical & electronic,materials science, multidisciplinary,physics, condensed matter, applied