Sintering behavior and microwave dielectric properties of Sr2CeO4 ceramics doped with Li2CO3-Bi2O3

Fuming Zhou,Hao Wang,Jianming Guo,Hui Yang,LingFeng Li,Qilong Zhang

DOI: https://doi.org/10.1007/s10854-020-04682-z

2020-10-23

Abstract:Microwave dielectric ceramics Sr₂CeO₄ + <i>n</i> wt% Li₂CO₃—Bi₂O₃ (LB) (1 ≤ <i>n</i> ≤ 4, L: B = <i>x</i>: <i>y</i>, weight ratio) were prepared by a traditional solid-state reaction method. The effects of LB additives on the phase formation, microstructure, sintering behavior, and microwave dielectric properties of Sr₂CeO₄ ceramics were investigated. The sintering temperature can be reduced obviously from 1270 to 950 °C because of the liquid phase formation of LB. Single-phase Sr₂CeO₄ ceramics with dense structure and homogenous grains were obtained by adding 1wt% LB. With LB content increasing, Q × f values would decrease because secondary-phase SrCeO₃ appeared in the ceramics. When the content of LB was fixed at 1 wt%, the sintering temperature and Q × f value would decrease simultaneously with the ratio of Li₂CO₃ increasing. Desirable performances of Sr₂CeO₄ + 1wt% LB ceramics: (<i>ε</i>_<i>r</i> = 14.36, Q × f = 102,023 GHz and <i>τ</i>_<i>f</i> =  − 66.42 ppm/°C, L:B = 2:8) and (<i>ε</i>_<i>r</i> = 13.56, Q × f = 70,109 GHz, τ_f =  − 64.17 ppm/°C, L:B = 8:2) can be achieved at 1075 °C and 950 °C, respectively, suggesting that Sr₂CeO₄–LB ceramics have a great potential for millimeter-wave applications.

engineering, electrical & electronic,materials science, multidisciplinary,physics, condensed matter, applied