The Sintering and Dielectric Properties Modification of Li2MgSiO4 Ceramic with Ni2+-ion Doping Based on Calculation and Experiment
Rui Peng,Hua Su,Di An,Yongcheng Lu,Zhihua Tao,Darning Chen,Liang Shi,Yuanxun Li
DOI: https://doi.org/10.1016/j.jmrt.2019.11.061
IF: 6.267
2020-01-01
Journal of Materials Research and Technology
Abstract:The microwave dielectric properties and sintering behavior of Li-2(Mg1-xNix)SiO4 (x=0.00-0.10) ceramics were researched with the help of first principle calculation and solid-state reaction experiment. The crystal structure, electron density, and formation energy were obtained through the density functional theory. The X-ray diffraction, scanning electron microscopy, energy-dispersive X-ray spectroscopy, and Network Analyzer were used in this study. The substitution of Ni2+-ion to Mg2+-ion could lower the densification temperature from 1250 degrees C to 1150 degrees C and improve the microwave dielectric properties of composite ceramics, demonstrated by the result of lattice parameters, bond population, electron density, and microstructure. A peak dielectric property of Li-2(Mg1-xNix)SiO4 (x=0.00-0.10) ceramics was achieved when x=0.04 (epsilon(r) = 5.69, Q x f = 28,448 GHz at 16 GHz, tau(f) = -15.3 ppm/degrees C) sintered at 1150 degrees C. Besides, LBBS glass was used as the sintering aid to lower the densification temperature from 1150 degrees down to 900 degrees. The Li-2(Mg0.96Ni0.04)SiO4 ceramic with 2 wt% LBBS sintered at 900 degrees C obtained excellent microwave dielectric properties, epsilon(r) = 5.89, Q x f = 29,320 GHz (at 16 GHz), tau(f) = -13.8 ppmPC, and there was no chemical reaction between the composite ceramics and Ag. It's a promising material for the applications of the millimeter-wave devices in the field of low temperature co-fired ceramics. (C) 2019 The Authors. Published by Elsevier B.V.