Influence of lithium modification on the properties of Y-doped Sr0.5Pb0.5TiO3 thermistors

Jingchang Zhao,Longtu Li,Zhilun Gui

DOI: https://doi.org/10.1016/S0924-4247(01)00714-2

2001-01-01

Abstract:Y-doped Sr0.5Pb0.5TiO3 ceramics with Li-modification were fabricated at relatively low sintering temperature. The sintered ceramics have novel nonlinear resistivity–temperature characteristics at the Curie temperature (Tc). As the Li concentration increases, sample’s room-temperature resistivities and positive temperature coefficient (PTC) (T>Tc) regularly increase. In addition, the samples exhibit obvious NTC–PTC composite effects at high concentration doping of lithium impurities. The samples’ morphologies and domain structures were investigated with scanning electron microscope (SEM) and transmission electron microscope (TEM) respectively, which reveal that Li additives are beneficial to the grain growth and the samples have simple 90°-domain structures inside the grains. The investigation of complex impedance spectroscopy demonstrates that the Li additives obviously increase the grain boundary resistances and decrease grain resistances, and the NTC–PTC composite effects of Li modified samples are originated from the grain boundaries.