The effect of lithium doping on the ferroelectric properties of LST ceramics

M.V. Zdorovets,A.L. Kozlovskiy

DOI: https://doi.org/10.1016/j.ceramint.2020.02.254

IF: 5.532

2020-07-01

Ceramics International

Abstract:The work is devoted to the study of the effect of lithium doping on the structural and electrical properties of ferroelectric ceramics LixSr1-xTiO3. The concentration of lithium dopant varied from x = 0.01 to 0.15. It was found that an increase in lithium during the synthesis leads to phase transformations of the type SrTiO3/TiO2 → SrTiO3/TiO2/Li2Ti3O7 → SrTiO3/Li2Ti3O7. According to the data obtained, the capacitance value for samples with a lithium content in the structure x = 0–0.01 is 0.05–0.07*10-9 F*cm-1, an increase in lithium concentration to x = 0.05–0.1 in the structure leads to an increase in the capacity value of 0.6*10-9 F*cm-1 with a further drop in the frequency range 103–105 Hz to 0.05–0.07*10-9 F*cm-1, and at a lithium concentration of x = 0.15, the capacitance increases sharply and retains its value throughout frequency range within the range of 0.9–1.2 0.05–0.07*10-9 F*cm-1. According to the data obtained, the deviation ΔT from the Curie-Weiss law for the studied ceramics is no more than 4, while the value of the Curie-Weiss constant is characteristic of ferroelectrics. The small value of ΔT indicates that for the initiation of phase transitions from tetragonal/orthorhombic to cubic at temperatures not exceeding 100–110 °C.

materials science, ceramics