Structure, dielectric response behavior and AC impedance spectroscopy of Ba0.95Ca0.05Zr0.3Ti0.7O3 ceramics with Li2CO3 addition for enhanced energy storage performance

Shiju Yang,Chao Feng,Hao Wang,Long Zhao,Jie Zhou,Huajun Sun,Xiaobin Xie

DOI: https://doi.org/10.1016/j.materresbull.2024.112705

IF: 5.6

2024-05-01

Materials Research Bulletin

Abstract:The low temperature sintering properties, structure and dielectric response behavior and AC impedance spectroscopy of Ba0.95Ca0.05Zr0.3Ti0.7O3+x wt.% Li2CO3 (x = 0 and x = 1.0) ceramic specimens were investigated. On this basis, the polarization (P) vs. electric field (E) relation characteristics and energy storage performance of the ceramic specimens were studied. The addition of Li2CO3 reduced the sintering densification temperature by 200 °C for the ceramic with x = 1.0, resulting in a relative density of 96.2 % after sintering at 1080 °C. Li+ incorporated into the B-site of the cubic perovskite-type and resulted in the formation of oxygen vacancy, which promoted the sintering densification process of ceramic samples with x = 1.0. The addition of lithium did not have remarkable adversely affecting on the basic dielectric properties, as the ceramic specimen with x = 1.0 sintered at 1080 °C exhibited a dielectric constant of 1950 and a loss of 0.4 % at 10 kHz. Additionally, the addition of lithium enhanced the energy storage performance of the specimens, with the maximum attainable electric field increasing by 50 % for the ceramic with x = 1.0 compared to the value for the ceramic with x = 0. The ceramic with x = 1.0 exhibited an energy storage density (ESD) of 1.0 J/cm3 and an efficiency of ∼80.0 % under 240 kV/cm, which was superior to the ceramic with x = 0. The enhanced energy storage performance of the ceramic with x = 1.0 (increased by ∼70 %) was tentatively explained with a strong restriction effect of the defect dipoles in the specimen to the electric field-driven motion of the oxygen vacancies in the specimen. Overall, these findings suggest that the addition of Li2CO3 could significantly improve the sintering and energy storage performance of BT-based dielectric ceramics, while did not result in remarkable negative impact on dielectric properties.

materials science, multidisciplinary