Abstract:Non-agglomerated nano-sized BaTiO3 powders were prepared by a 3 step decomposition of barium titanyl citric acid chelate derived from Ba(NO3)2-TiO(NO3)2-citric acid-NH4NO3 based complex compound system. The 1st step was the thermal treatment of chelate wet gel at 150°C for 40min to remove water and non-bridging hydroxyl groups and to form expanded gel intermediate. The 2nd step was the decomposition of the organic fuel by igniting expanded gel intermediate at 300°C. The 3rd step was the formation of the high purity BaTiO3 by calcining the decomposed powders at 700°C for 2 hours. The most expanded gel intermediate was found to be a decisive factor for the elimination of hard agglomerate. In addition, the initial oxidant/fuel molar ratio was shown to strongly influence the characteristics of the powders thus obtained. The optimum oxidant/fuel value was 3 for obtaining non-agglomerated pure BaTiO3 powders with a particle size of 50 nm. The agglomerate degree of BaTiO3 powders was determined by particle morphology and uniformity of the green compact microstructure observed by field emission scanning electron microscopy and scanning electron microscope.

Synthesis of BaTio3 nanocrystals by stearic acid gel method

Synthesis of (bi0.5na0.5)tio3 Nanocrystalline Powders by Stearic Acid Gel Method

Preparation of Single-Crystalline BaTi5O11 Nanocrystals by Hydrothermal Method

PREPARATION AND SINTERING PROPERTIES OF BaTi4O9 BY CITRIC ACID GEL METHOD

Room-Temperature Synthesis of BaTiO<sub>3</sub>Nanoparticles in Large Batches

The Preparation of Barium Ferrite Nanocrystalline Powders by A Stearic Acid Gel Method

Ba 4 Ti 13 O 30 Nanocrystals Prepared by Hydrothermal Method

Citric Acid Gel Method Synthesis, Characterization And Dielectric Properties Of Single-Phase Bati4o9

Barium Titanate Prepared by Stearic Acid-Gel Method

Composition and shape control of single-crystalline Ba1-xSrxTiO3 (x=0-1) nanocrystals via a solvothermal route

Size-controlled synthesis of BaTiO3 nanocrystals via a hydrothermal route

Synthesis of Nanocrystalline 0.94Bi(0.5)na(0.5)tio(3)-0.06Batio(3) Powder by A Citrate Method

Synthesis of Nanocrystalline 0.94Bi<sub>0.5</sub>Na<sub>0.5</sub>TiO<sub>3</sub>-0.06BaTiO<sub>3</sub> Powder by a Citrate Method

Synthesis of Highly Dispersed Barium Titanate Nanoparticles by a Novel Solvothermal Method

Preparation of A Monodispersed Suspension of Barium Titanate Nanoparticles and Electrophoretic Deposition of Thin Films

Preparation of barium strontium titanate Ba(1-x)Sr(x)TiO(3) (0<or= x <or=0.2) single-crystal nanorods by a novel combined method

Sol–gel based synthesis of ultrafine tetragonal BaTiO 3

Study on peculiar properties of nanocrystalline BaTiO3 powder and ceramics

Low-temperature Synthesis of TiB2 Nanocrystals Using TiO2 ,LiBH4 and Mg

Process for Non-Agglomerated Nanometer-Sized Barium Titanate Powders by Sol-Gel Auto-Igniting Synthesis

Preparation of Nanoscaled BaTiO3 Powders by DSS Method Near Room Temperature under Normal Pressure