Abstract:An ultrafine barium ferrite powder of high coercivity and high saturation magnetization has been successfully prepared from an inverse water-in-oil microemulsion consisting of cyclohexane, NP5/NP9, and an aqueous solution of mixed ferric nitrate and barium nitrate. An ammonium hydroxide solution was used as the precipitant to obtain the hydroxide precursor of particle size in the range of 10–30nm from the microemulsion. The resulting precursor is characterized using techniques such as thermogravimetric analysis (TGA), differential thermal analysis (DTA) and a FT-IR analyzer. It was then calcined at various temperatures ranging from 600 to 950°C in order to develop the designed barium ferrite phase. Phase development in the precursor at each calcination temperature was monitored using X-ray diffractometer and a 57Fe-Mössbauer spectrometer analyzer. The particle size and size distribution of the calcined powders were determined using light scattering technique, scanning electron microscope and a transmission electron microscope. A high purity barium ferrite was obtained when the precursor was calcined at 950°C for 4h. It exhibits an intrinsic coercivity (iHc) of 5639Oe and a saturation magnetization (Ms) of 69.7emu/g, when characterized using a vibrating sample magnetometer (VSM).

The Preparation of Barium Ferrite Nanocrystalline Powders by A Stearic Acid Gel Method

Synthesis of Nanocrystalline Ferrites Zn0.4ni0.6cr0.5laxfe1.5-Xo4 and Its Magnetic Properties

Preparation and Magnetic Properties of BaZn2−xCoxFe16O27 Nanocrystalline Powders by the Stearic Acid Gel Method

Preparation and Magnetic Properties of Barium Hexaferrite Nanoparticles Produced by the Citrate Process

PREPARATION AND SINTERING PROPERTIES OF BaTi4O9 BY CITRIC ACID GEL METHOD

Synthesis and characterization of X-type barium ferrite nanocrystals

Preparation and magnetic properties of BaFe12-2x(CoT)xO19 ultrafine particles

Synthesis of BaTio3 nanocrystals by stearic acid gel method

The Characterization and Preparation of Nano-Scale Fe Doping Tio2 by Sol-Gel Method (I) - the Crystallization and Thermal Decomposition Process of Fe Doping Tio2 Xerogel Powders Using Thermal Tg-Ir Spectrometry

Influence of Different Preparation Methods on Crystallisation and Morphology of Fe2o3 Nanoparticles

Preparation of barium sulfate submicro-particles with high purity by solventing-out process

Preparation of A Monodispersed Suspension of Barium Titanate Nanoparticles and Electrophoretic Deposition of Thin Films

Barium Titanate Prepared by Stearic Acid-Gel Method

Key Step in Synthesis of Ultrafine BaFe12O19 by Sol-Gel Technique

An Ultrafine Barium Ferrite Powder of High Coercivity from Water-In-Oil Microemulsion

Citric Acid Gel Method Synthesis, Characterization And Dielectric Properties Of Single-Phase Bati4o9

Preparation of Ti Doped BaFe12O19 Ceramics by a Sol-Gel Process

Preparation of the Percolative Nickel-Zinc Ferrite/Barium Titanate Composite Ceramics with Liquid-Solid Hybrid Method

Study on peculiar properties of nanocrystalline BaTiO3 powder and ceramics

Size-controlled synthesis of BaTiO3 nanocrystals via a hydrothermal route

Room-Temperature Synthesis of BaTiO<sub>3</sub>Nanoparticles in Large Batches