Abstract:Hexagonal ferrites of M -type (in particular, BaFe 12 O 19 ) are magnetic materials with functional characteristics affected both by chemical composition and technology of their synthesis. We present the results of studying the magnetic and structural properties of BaFe 12 – x Cu x O 19 hexaferrites ( x = 0, 0.1, 0.2, 0.3, 0.4) obtained by hydrothermal synthesis with partial substitution of copper for iron. The composition of the synthesized samples was analyzed using X-ray diffraction, and the magnetic characteristics were measured using a vibration magnetometer. It has been revealed that the coercivity of the ferrite powders depends non-monotonically on the copper concentration and reaches the maximum (5629 Oe) and minimum (4698 Oe) values at x = 0 and x = 0.2. The presence of copper reduces the coercive force, but at the same time the values remain rather high compared to the results of similar studies. The saturation magnetization of the obtained ferrites gradually decreases (from 65.88 to 60.75 A · m 2 /kg at x = 0 and x = 0.4, respectively) with increasing. The distribution of Cu over ferrite sublattices was studied using Mössbauer spectroscopy. It is shown that in the hexaferrite structure, copper ions preferentially occupy 12 k and 4 f 1 sites. Hence, a decrease in the saturation magnetization with increasing x is most likely attributed to the presence of side non-magnetic phases observed on X-ray diffraction patterns. It is also revealed that during synthesis, copper participates in the formation of low-melting phases on the surface of hexaferrite grains which promotes agglomeration of the particles. Thus, the resulting powders can potentially be sintered at lower temperatures and, therefore, without a significant increase in the size of crystallites. Herewith, the coercivity retains its original high values. The results obtained can be used in developing ferrite permanent magnets with improved characteristics.

Preparation and magnetic properties of BaFe12-2x(CoT)xO19 ultrafine particles

Synthesis and Characterization of Nanocrystalline BaFe9.6Co0.8Ti0.8M0.8O19 Particles

Preparation of Ti Doped BaFe12O19 Ceramics by a Sol-Gel Process

The Preparation of Barium Ferrite Nanocrystalline Powders by A Stearic Acid Gel Method

Structure And Magnetic Properties Of Co2.73fe0.27o4 Synthesized By The Heat-Decomposition Method

Preparation and Magnetic Properties of Barium Hexaferrite Nanoparticles Produced by the Citrate Process

Synthesis and characterization of X-type barium ferrite nanocrystals

Preparation and characterizations of ultrafine hexaganoal ferrite Co2Z powders

Preparation and Magnetic Properties of BaZn2−xCoxFe16O27 Nanocrystalline Powders by the Stearic Acid Gel Method

Formation of BaFe12-xNixO19 Ceramics with Considerably High Dielectric and Magnetic Property Coexistence

An Ultrafine Barium Ferrite Powder of High Coercivity from Water-In-Oil Microemulsion

Extra up-spin magnetic moments and extraordinary high saturation magnetization of Ni2+ doped barium ferrite in 4f(2) site

Synthesis and Magnetic Properties of Single-Crystalline BaFe12O19 Nanoparticles

Key Step in Synthesis of Ultrafine BaFe12O19 by Sol-Gel Technique

A study on the preparation and magnetic properties of Fe100−xBx ultrafine amorphous powders

Exploring structural, magnetic and dielectric properties of Ba1−xCoxFe12O19 hexaferrites

Improving the Magnetic Properties of Hydrothermally Synthesized Barium Ferrite

Study of the magnetic and structural properties of BaFe12 – xCuxO19 ferrites obtained by hydrothermal synthesis

Influence of CoFe2O4 particle size on the development of in-situ phases and magnetic properties of ex-situ combustion derived ferrite-BaTiO3 composite

Sol–gel Synthesis, Magnetic and Magneto-Optical Properties of CoFe2−xTbxO4 Nanocrystalline Films

Fe or Ni–Fe Alloy Coated Barium Ferrite Particles