An Ultrafine Barium Ferrite Powder of High Coercivity from Water-In-Oil Microemulsion

XY Liu,J Wang,LN Gan,SC Ng,J Ding

DOI: https://doi.org/10.1016/s0304-8853(97)01141-4

IF: 3.097

1998-01-01

Journal of Magnetism and Magnetic Materials

Abstract:An ultrafine barium ferrite powder of high coercivity and high saturation magnetization has been successfully prepared from an inverse water-in-oil microemulsion consisting of cyclohexane, NP5/NP9, and an aqueous solution of mixed ferric nitrate and barium nitrate. An ammonium hydroxide solution was used as the precipitant to obtain the hydroxide precursor of particle size in the range of 10–30nm from the microemulsion. The resulting precursor is characterized using techniques such as thermogravimetric analysis (TGA), differential thermal analysis (DTA) and a FT-IR analyzer. It was then calcined at various temperatures ranging from 600 to 950°C in order to develop the designed barium ferrite phase. Phase development in the precursor at each calcination temperature was monitored using X-ray diffractometer and a 57Fe-Mössbauer spectrometer analyzer. The particle size and size distribution of the calcined powders were determined using light scattering technique, scanning electron microscope and a transmission electron microscope. A high purity barium ferrite was obtained when the precursor was calcined at 950°C for 4h. It exhibits an intrinsic coercivity (iHc) of 5639Oe and a saturation magnetization (Ms) of 69.7emu/g, when characterized using a vibrating sample magnetometer (VSM).