Study on Preparation of Nano-Fe2O3 by Thermal-Crystallization Method
Shi Peiyang,Zhang Ying,Liu Chengjun,Jiang Maofa
DOI: https://doi.org/10.3321/j.issn:1002-185x.2007.z2.222
2007-01-01
Rare Metal Materials and Engineering
Abstract:Nano-Fe2O3 was synthesized from FeSO4 by hydrothermal method, using polyethylene glycol as dissolvent and NH3H2O as precipitating agent. It was characterized by XRD and SEM. The results showed that, as increasing of pH value from 6 to 10, reaction time was shortened from 90 min to 30 min, crystal morphology was changed from grainy crystal to flaky crystal, and the color of samples became fuscous. When reaction temperature increased from 140 degrees C to 170 degrees C, reaction time was shortened from 90 min to 45 min. The average crystal granularity increased from 50 nm to 800 nm, and crystal uniformity descended. Crystal morphology was changed from spherocrystal to acicular crystal, and the color of samples reddened gradually. On the experimental condition, the optimal pH, hydrothermal temperature and hydrothermal time were 7, 160 degrees C and 60min, respectively.