Abstract:By using Fe(NO3)3·9H2O as the starting materials,caustic potash as the mineralizer,α-FeOOH nanowires were prepared by hydrothermal method.The phase and micro-morphology of the products were characterized by X-ray diffraction (XRD),transmission electron microscopy(TEM) and selected area electron diffraction(SAED).The effects of mineralizer concentration and reaction temperature on the phase formation and morphology were investigated.Results indicated that αFeOOH nanowires with orthorhombic structure could be successfully synthesized via hydrothermal processing with 0.1 mol/L KOH at 100 ℃ for 6 h.With the increase of mineralizer concentration,α-FeOOH phase decreases and hexagonal α-Fe2O3 phase appears.When mineralizer concentration is 2.0 mol/L,no crystal phase is obtained.There is no effect of mineralizer concentration on the crystal structure of products at low temperature(40 ℃),for only amorphous phase is obtained under various concentration.At high temperature(200 ℃),α-FeOOH phase can be converted into hexagonal α-Fe2O3 phase rapidly and the size of α-Fe2O3 becomes larger with the increase of mineralizer concentration.

Synthesis and phase formation mechanism of alpha-Fe2O3 powders by hydrothermal reaction method

Effects of KOH and Temperature on Hydrothermal Synthesis of Α-Feooh Nanowire

Hydrothermal Synthesis and Characterization of Uniform Α-Feooh Nanowires in High Yield

Hydrothermal synthesis of monodisperse α-Fe2O3 nanocubes

Research on the mechanism of the formation of nanoparticle of α-Fe2O3 powder in aqueous solution with amorphous δ-FeOOH

Hydrothermal Synthesis of Fe2O3 with Different Nanostructures

Solvothermal Synthesis and Magnetic Property of Monodispersed Fe_3O_4 Nano-powders

Hydrothermal Synthesis And Characterization Of Single-Crystalline Alpha-Fe2o3 Nanocubes

Hydrothermal Preparation of CuAlO2 Powder

Synthesis Of Fe-Doping Aluminum Titanate Powders

Hydrothermal synthesis and characterization of α-FeOOH and α-Fe2O3 uniform nanocrystallines

Hydrothermal synthesis and characterization of monodisperse α-Fe2O3 nanocubes

Selective Synthesis Of Alpha-Feooh And Alpha-Fe2o3 Nanorods Via A Temperature Controlled Process

The Synthesis of Monodispersed Α-Fe2o3 Nanoparticles Via a Hydrothermal Process

Synthesis and magnetic properties of γ-Fe2O3/SiO2 core–shell nanoparticles under hydrothermal conditions

Preparation and Characterization of Α-Fe2o3 from Iron Mud by Hydrothermal Synthesis

Hydrothermal Synthesis and Characterization of Nanocrystalline Gamma-Fe2o3 Particles

Formation of α-Fe2O3/FeOOH nanostructures with various morphologies by a hydrothermal route and their photocatalytic properties

Preparation ofα-Fe2O3 nanoparticles by hydrolysis precipitation method

Hydrothermal synthesis and magnetic properties of α-Fe 2O 3 polyhedrons

Morphology-controlled Synthesis of Α-Feooh and Its Derivatives