Abstract:Intrinsically poor reactivity restricts pure hematite (α-Fe2O3) from practical photo-Fenton-like systems. Surface structure engineering is considered one of effective methods to tune its photo-Fenton-like catalytic performance. Therefore, it is essential to understand how the surface structure of α-Fe2O3-based photocatalysts alters its catalytic activity at the nanoscale. Herein, four α-Fe2O3-x materials with different morphologies (sphere, octahedron, spindle and rod) and controllable oxygen vacancies (OVs) were synthesized with benzimidazole (BIm)-modified Fe-MOFs (MOFs = metal organic frameworks) as templates using the solvothermal method. The rod-like α-Fe2O3-x was found to exhibit the highest activity for the complete methylene blue (MB) degradation with apparent reaction rate constant k =0.08 min-1. While apparent reaction rate constants for α-Fe2O3-x with sphere-, octahedron- and spindle-like morphologies are only 0.02, 0.035 and 0.05 min-1, respectively. The enhanced photocatalytic activity can be attributed to the synergy of large surface area, high Fe2+ and OVs concentrations. This is further substantiated by density functional theory (DFT) calculations, which indicates that both Fe2+ and OVs facilitate H2O2 dissociation to produce hydroxylradicals (•OH) for MB degradation. The present work provides a promising strategy for designing low-cost and efficient α-Fe2O3-based photocatalysts with abundant OVs for photo-Fenton-like catalysis and other energy and environmental applications.

Formation of α-Fe2O3/FeOOH nanostructures with various morphologies by a hydrothermal route and their photocatalytic properties

Controllable hydrothermal synthesis, optical and photocatalytic properties of TiO 2 nanostructures

Facile synthesis of hierarchical Ag 3 PO 4 /TiO 2 nanofiber heterostructures with highly enhanced visible light photocatalytic properties

Synthesis and phase formation mechanism of alpha-Fe2O3 powders by hydrothermal reaction method

Hydrothermal preparation of α-Fe2O3 nano-scale spheres and their photocatalytic property study

Synthesis, Characterization and Photocatalytic Activity of Hierarchical Spherical TiO2 Nanostructures

Preparation and Catalytic Property of Single Crystal Multiporousα-Fe_2O_3 Nanorods

Hydrothermal synthesis and characterization of α-FeOOH and α-Fe2O3 uniform nanocrystallines

Single-crystalline Α-Fe2o3 Nanostructures: Controlled Synthesis and High-Index Plane-Enhanced Photodegradation by Visible Light

A Novel Delafossite Structured Visible-Light Sensitive AgFeO2 Photocatalyst: Preparation, Photocatalytic Properties, and Reaction Mechanism

Synthesis of Small Yolk–shell Fe3O4@TiO2 Nanoparticles with Controllable Thickness As Recyclable Photocatalysts

Morphology-controlled Synthesis of Α-Feooh and Its Derivatives

Effects of KOH and Temperature on Hydrothermal Synthesis of Α-Feooh Nanowire

One-pot Hydrothermal Synthesis of the Dual-Phase Anatase/tio2-B Nanoparticles with K2Ti6O13 Nanofibers for Enhanced Photocatalysis

Low‐Temperature Transformation of Titania Thin Films from Amorphous Nanowires to Crystallized Nanoflowers for Heterogeneous Photocatalysis

Morphology controlled synthesis of α-Fe2O3-x with benzimidazole-modified Fe-MOFs for enhanced photo-Fenton-like catalysis

Preparation and Photocatalytic Activity of TiO<sub>2</sub>/Fe<sub>2</sub>O<sub>3 &Lt;/sub>nanocomposite

Hydrothermal Synthesis, Photocatalytic and Magnetic Properties of Pure-Phase Bi2Fe4O9 Microstructures

Hydrothermal synthesis of monodisperse α-Fe2O3 nanocubes

Selective Synthesis Of Alpha-Feooh And Alpha-Fe2o3 Nanorods Via A Temperature Controlled Process

Α-Fe2o3 Nanocrystals: Controllable SSA-Assisted Hydrothermal Synthesis, Growth Mechanism, and Magnetic Properties