Hydrothermal Conversion of Fe2o3/Sio2 Spheres into Fe2o3/Silicalite-1 Nanowires: Synthesis, Characterization, and Catalytic Properties
Pengfei Xie,Lifeng Chen,Zhen Ma,Chengyun Huang,Zhiwei Huang,Yinghong Yue,Weiming Hua,Yi Tang,Zi Gao
DOI: https://doi.org/10.1016/j.micromeso.2014.08.020
IF: 5.876
2014-01-01
Microporous and Mesoporous Materials
Abstract:Fe2O3 nanoparticles were dispersed onto SiO2 by impregnating amorphous SiO2 spheres with Fe(NO3)(3) followed by spray drying and calcination. Interestingly, the amorphous SiO2 spheres in the sample could be converted into Silicalite-1 nanowires after being hydrothermally treated in the presence of a mixture of ethylenediamine and triethylamine (dual templates) for over 4 days, whereas the Fe2O3 nanoparticles were still highly dispersed on the formed Silicalite-1 nanowires. Meanwhile, a fraction of Fe(III) species entered the zeolitic framework. Relevant characterization was conducted using X-ray fluorescence (XRF), N-2 adsorption-desorption, X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), ultraviolet-visible (UV-Vis) spectroscopy, electron paramagnetic resonance (ESR), X-ray photoelectron spectroscopy (XPS), and H-2-temperature-programmed reduction (H-2-TFR). The catalytic properties of the samples were studied using CO oxidation, N2O decomposition, and selective reduction of NO as probe reactions. (C) 2014 Elsevier Inc. All rights reserved.