Abstract:We prepared the magnetic nanoparticles of Fe3O4from thermal decomposition of the Fe oleates precursors synthesized by iron chlorides and sodium oleate,and the SiO2-coated Fe3O4nanoparticles by combining the reverse microemulsion and organic template methods. FTIR was adopted to investigate the surface of Fe oleate under different treatments,and the growth of Fe3O4 nanoparticles with different reactant concentrations of oleic acid and heating rates. The results indicated that the superficial oleic acid of the waxy solid Fe oleates after extraction from ethanol and acetone was partially removed,which impairs the formation of monodispersion Fe3O4 naoparticles. The effect of heating rate on the growth of nanoparticles was weak compared with that of the concentration of Fe oleates. When the concentration of oleic acid is 0.09 mol/L, a characteristic peak of Fe3O4 at 576 cm-1(assignable to the bending vibrations of Fe-O) is enhanced significantly. The XRD (X-ray diffraction) spectra,TEM (transmission electron microscopy) images and SQUID (superconducting quantum interference device) confirmed that the Fe3O4 nanoparticles are spinel cubic crystal and have a good monodispersity and super-paramagnetism. Whats more,the TEM of SiO2-coated Fe3O4 nanoparticles also confirmed that the Fe3O4 nanoparticles were well coated by mesoporous SiO2.

Preparation and Surface Modification of Monodisperse Fe3O4 Nanoparticles

Preparation and Surface Modification of Magnetic Fe3O4 Nanoparticles

Preparation and Surface Modification of Fe<sub>3</sub>O<sub>4 &Lt;/sub>nano-Magnetic Powders

Synthesis of Monodispersed Fe3O4 Magnetite Nanoparticles by ethylene glycol solvothermal method

Preparation and surface modification of magnetic nano-Fe_3O_4

Preparation, Surface Functionalization and Application of Fe3O4 Magnetic Nanoparticles

Polyol Synthesis of Superparamagnetic Fe_3O_4 Nanoparticles for Magnetic Resonance Imaging

Research Progress on Preparation and Surface Modification of Fe3O4 Magnetic Nano-particles

Surface Modification of Fe3O4 Nano Particles and Its Applications in Preparation of Magnetic Alumina Catalyst Supports

Preparation and Characterization of Magnetic Nanoparticles of Fe-3 O-4 Coated with Mesoporous Sio2

Preparation and Characterization of Monodispersed Fe3O4 Sub-microspheres

Synthesis of Fe3O4 Nanoparticles and Their Magnetic Properties

Preparation and characterization of monodispersed Fe3O 4 sub-microspheres | Preparation and characterization of monodispersed Fe3O 4 sub-microspheres

Synthesis of Fe3O4 Nanoparticles and Preparation of Magnetic Fluids

Preparation and Characterization of Monodispersed Fe_3O_4 Sub-microspheres

Solvothermal synthesis and characterization of size-controlled monodisperse Fe 3 O 4 nanoparticles

Preparation of Nearly Monodispersed Fe3O4/SiO2 Composite Particles from Aggregates of Fe3O4 Nanoparticles

Preparation and Characterization of Silica-Coated Fe3O4 Nanoparticles Used As Precursor of Ferrofluids

Synthesis and Characterization of Monodisperse Fe3O4Nanospheres with Uniform Particle Size Distribution by a Simple Solvothermal Method

Synthesis of Fe3O4 Nanoparticles by Co-precipitation and Micro-reactor Method