Abstract:The present work reports the preparation of stable polydimethylsiloxane (PDMS)-based magnetic fluid with Fe3O4 3 O 4 magnetic nanoparticle dispersion. The Fe3O4 3 O 4 nanoparticles are modified by the silane coupling agent (SCA) to form a hydroxyl-alkane layer, which provides hydrogen bonding sites. The amino-silicone molecules of surfactant are adsorbed on the particle surface through hydrogen bonds and formed a polymer layer, ensuring good suspension of particles and stability of composed magnetic fluid. The crystal and chemical structures of modified particles were characterized by X-ray diffraction (XRD) and Fourier transform infrared spectroscopy (FT-IR). The morphology and coating status of the particles were observed using high resolution transmission electron microscope (HRTEM). The images confirmed an average particle size of 10 nm and single-domain Fe3O4 3 O 4 phase. The volatilization rate of the magnetic fluid at 80 degrees C under vacuum reached 1.4*10-4-4 g/cm2 & sdot;h 2 & sdot;h while maintaining good fluidity at-55 degrees C. Thermostability and magnetic properties were determined by thermal gravimetric analyzer (TGA) and vibrating sample magnetometer (VSM). The material demonstrates super- paramagnetic behavior due to the particle diameter being below the critical size (Dc). c ). The rheological properties of magnetic fluid were investigated, along with the impact of surfactant viscosity on these properties. The magneto-viscous effect and polymer-like characteristics imparted by surfactant molecular chains significantly influence the non-Newtonian behavior. Surfactant molecules alter the magnetorheological response by influencing the formation of field-induced particle structures.

Preparation and characterization of water-soluble monodisperse magnetic iron oxide nanoparticles via surface double-exchange with DMSA

Magnetic Fe3O4 Nanoparticles: Synthesis and Application in Water Treatment

Preparation of Water-Soluble Magnetite Nanocrystals Through Hydrothermal Approach

Polyol Synthesis of Superparamagnetic Fe_3O_4 Nanoparticles for Magnetic Resonance Imaging

Synthesis of Monodispersed Fe3O4 Magnetite Nanoparticles by ethylene glycol solvothermal method

In Situ Precipitation: a Novel Approach for Preparation of Iron-Oxide Magnetoliposomes.

Preparation and Surface Modification of Monodisperse Fe3O4 Nanoparticles

Synthesis and characterization of stable water-soluble Fe3O4 nanoparticles

Synthesis of Water-soluble Fe3O4 Nanocrystals with a Phase-transfer Method

Magnetite Fe3O4 Nanoparticles and Hematite Α-Fe2o3 Uniform Oblique Hexagonal Microdisks, Drum-Like Particles and Spindles and Their Magnetic Properties

Influence of Morphology and Surface Exchange Reaction on Magnetic Properties of Monodisperse Magnetite Nanoparticles

Facile Method to Synthesize Oleic Acid-Capped Magnetite Nanoparticles

Stability of hydrophilic magnetic nanoparticles under biologically relevant conditions.

Solid-state Synthesis of Monocrystalline Iron Oxide Nanoparticle Based Ferrofluid Suitable for Magnetic Resonance Imaging Contrast Application

Stabilized Bare Superparamagnetic Iron Oxide Nanoparticles: Synthesis and Characterization

Magnetic Monodisperse Fe3o4 Nanoparticles

The Synthesis and Characterization of Poly(st-Dvb-maa) Coated Iron Oxide Microspheres with Large Diameter and Narrow Distribution

Facile Synthesis of Size-Controllable Monodispersed Ferrite Nanospheres

Synthesis of N-Hexadecylphosphonic Acid-Coated Monodisperse Fe3O4 Superparamagnetic Nanoparticles

In Situ Preparation of Magnetic Chitosan/fe3o4 Composite Nanoparticles in Tiny Pools of Water-in-oil Microemulsion

Preparation and Characterization of Polydimethylsiloxane Based Magnetic Fluid