Influential factors of preparing hollow superparamagnetic Fe3O4 nanospheres
Jian Peng,Qi Tang,Yi-feng Pan,Jing-bo Tang,Bo Li,Wei Chen,Jian Cui,Yang-de Zhang
DOI: https://doi.org/10.3969/j.issn.1673-8225.2010.25.014
2010-01-01
Abstract:BACKGROUND:Hollow microspheres exhibit good biocompatibility and have been widely used in many fields such as biomedicine and chemistry.OBJECTIVE:To study the affecting factors including the reaction temperature,reaction time,the number of washing,ultrasonic time in preparation process conditions on the particle size of hollow superparamagnetic Fe3O4 nanospheres.METHODS:With polyoxyethylene-polyoxypropylene-polyoxyethylene-block copolymer F127 as raw materials,Fe3O4 hollow superparamagnetic nanospheres were prepared by coprecipitation methods.Using mathematical methods of orthogonal experiment,a 4 × 3 orthogonal experimental model was designed.The influence of different preparation conditions such as the reaction temperature,reaction time,the number of washing and ultrasonic time,on the size of hollow magnetic nanoparticles was determined.RESULTS AND CONCLUSION:The optimal preparation conditions were:75 ℃,fully reacting 6 hours,washing three times using methanol/deionized water,30% power ultrasonic treatment for 20 minutes.After filtration by a 0.22-μm filter,the samples were characterized by particle size analyzer,X-ray diffraction and transmission electron microscopy.The average diameter of Fe3O4 hollow magnetic nanospheres was 37.5 nm,shell thickness was about 10 nm,particle size and distribution were even.