Abstract:Superparamagnetic Fe 3O 4 nanoparticles were synthesized via a modified coprecipitation method, and were characterized with X-ray diffraction (XRD), vibrating sample magnetometer (VSM), Zeta potential and FT-IR, respectively. The influences of different kinds of surfactants (sodium dodecyl benzene sulfonate, polyethyleneglycol, oleic acid and dextran), temperatures and pH values on the grain size and properties were also investigated. In this method, Fe 3+ was used as the only Fe source and partially reduced to Fe 2+ by the reducing agent with precise content. The following reaction between Fe 3+, Fe 2+ and hydroxide radical brought pure Fe 3O 4 nanoparticles. The tiny fresh nanoparticles were coated in situ with surfactant under the action of sonication. Comparing with uncoated sample, the mean grain size and saturation magnetization of coated Fe 3O 4 nanoparticles decrease from 18.4 nm to 5.9-9.0 nm, and from 63.89 emu g -1 to 52-58 emu g -1 respectively. When oleic was used as the surfactant, the mean grain size of Fe 3O 4 nanoparticles firstly decreases with the increase of reaction temperature, but when the temperature is exceed to 80 °C, the continuous increase of temperature resulted in larger nanoparticles. the grain size decreases gradually with the increasing of pH values, and it remains unchanged when the PH value is up to 11. The saturation magnetization of as-prepared Fe 3O 4 nanoparticles always decreases with the fall of grain size. © 2011 Elsevier B.V. All rights reserved.

Effect of ferric ions on the morphology and size of magnetite nanocrystals synthesized by ultrasonic irradiation

Influence of Different Preparation Methods on Crystallisation and Morphology of Fe2o3 Nanoparticles

Effect of reaction condition on microstructure and properties of (NiCuZn)Fe2O4 nanoparticles synthesized via co-precipitation with ultrasonic irradiation

Rapid growth of magnetite nanoplates by ultrasonic irradiation at low temperature

The Effect of [fe 3+ ]/[fe 2+ ] Molar Ratio and Iron Salts Concentration on the Properties of Superparamagnetic Iron Oxide Nanoparticles in the Water/ethanol/toluene System

Influence of synthesis conditions on the structure and size of magnetite nanoparticles in co-precipitation method without stabilizer in one system

Synthesis of Mn–Zn Ferrite Nanoparticles by the Coupling Effect of Ultrasonic Irradiation and Mechanical Forces

"Synthesis and Optimization of Cubic Shaped Magnetite Nanoparticles by One-Step Ultrasound Irradiation Process"

Single-crystalline Fe3O4 Nanosheets: Facile Sonochemical Synthesis, Evaluation and Magnetic Properties

Ultrasonic-assisted Preparation of Monodisperse Iron Oxide Nanoparticles

Size Controlled and Morphology Tuned Fabrication of Fe3O4 Nanocrystals and Their Magnetic Properties

Synthesis And Characterization Of Magnetite Particles By Co-Precipitation Method

Effect of Ultrasonic Treatment on the Magnetization Enhancement of Fe 3 O 4 Nanocrystallines

Size Controllable Synthesis of Magnetite Fe3O4 Nanoparticles

Facile shape and size-controlled growth of uniform magnetite and hematite nanocrystals with tunable properties

Microemulsion Synthesis and Characterization of Nano-Fe3O4Particles and Fe3O4Nanocrystalline

Synthesis and Study of Fe3O4 Magnetic Particles with High Saturation Magnetization

Ultrasonic-assisted in situ synthesis and characterization of superparamagnetic Fe 3O 4 nanoparticles

Preparation and Characterization of Superparamagnetic Fe<sub>3</sub>O<sub>4</sub> Nanoparticles with Controlled Sizes

Effects on Direct Synthesis of Large Scale Mono-Disperse Ni0.5zn0.5fe2o4 Nanosized Particles

Effects of Amount of Benzyl Ether and Reaction Time on the Shape and Magnetic Properties of Fe3o4 Nanocrystals