Quantification of surface orientation effect on the thermal stability of γ-Al2O3 with different morphologies
Hao Feng,Hao Wang,Zhejie Ma,Shiyao Wang,Ping Li
DOI: https://doi.org/10.1016/j.apsusc.2022.153509
IF: 6.7
2022-08-01
Applied Surface Science
Abstract:Three types of γ-Al2O3 materials with morphologies as cluster, nanorod, and nanoplate, respectively, were prepared by hydrothermal synthesis of the corresponding boehmites as the precursors and subsequent calcination at 600 °C. The surface orientations of the γ-Al2O3 materials were identified using the characterization techniques of XRD, TEM and SAEDto quantify the morphologies. To assess the thermal stability of different Al2O3 materials, the phase compositions and the specific surface areas changing with temperature in 600–1200 °C were analyzed. The results show that the transformation of Al2O3 from γ- to δ-, θ-, and finally to α-phase is remarkably diverse for different Al2O3, which is more dependent on the surface orientation rather than the primary crystal size of the material. The variation of total surface energy of each surface-oriented Al2O3 with the temperature demonstrates its own regularity when taking the phase composition and the crystal plane proportion into account. The Nanorod Al2O3 benefits from its large proportion of (100)δ||(001)θ planes featured with low surface energies, giving rise to large surface area (92.5 m2/g) at 1000 °C. In contrast, the Cluster sample contains the least α-Al2O3 at 1200 °C, suggesting its high thermal stability, but concomitant with significant loss in surface area.
chemistry, physical,physics, applied, condensed matter,materials science, coatings & films