Abstract:The microstructure of BaTiO3 (BT) nanocrystals was investigated by X-ray diffraction (XRD), scanning electron microscopy (SEM), selected area electron diffraction (SAED), and (high-resolution) transmission electron microscopy [(HR)TEM]. The BT nanocrystals have a cubic perovskite structure as revealed by XRD and SAED. They were prepared by a hydrothermal method using different starting materials: (i) Using as-prepared titanium hydroxide and barium hydroxide as starting materials, BT nanocrystals were obtained with a narrow size distribution and an average grain size of 65 nm, exhibiting a spherical particle morphology and smooth surfaces. These nanocrystals showed almost uniform contrast in TEM. HRTEM lattice fringe images indicate a rather uniform, perfect crystal structure. (ii) Using barium hydroxide and titanium dioxide (anatase) as starting materials, many coarse-faceted cubic nanocrystals and a small amount of spherical particle were observed, indicating a developed bimodal size distribution. Diffraction contrast variations across these particles indicate the presence of high strain in these BT particles. The strain is probably caused by the lattice defects like OH− ions and their compensation by cation vacancies. HRTEM images demonstrated that (1 0 0) and (1 1 0) surface facets are present on these particles. In addition they revealed the presence of very small-nucleated BT islands at the edges of the faceted particles.

Formation mechanism of BaTiO3nanocrystalline synthesized at room temperature

Room-Temperature Synthesis of BaTiO<sub>3</sub>Nanoparticles in Large Batches

Size-controlled synthesis of BaTiO3 nanocrystals via a hydrothermal route

Preparation of Single-Crystalline BaTi5O11 Nanocrystals by Hydrothermal Method

Low-temperature Synthesis of TiB2 Nanocrystals Using TiO2 ,LiBH4 and Mg

Direct Synthesis of Ultrafine Tetragonal BaTiO3 Nanoparticles at Room Temperature

Room temperature synthesis of BaTiO3 nanoparticles using titanium bis(ammonium lactato) dihydroxide

Preparation of Nanoscaled BaTiO3 Powders by DSS Method Near Room Temperature under Normal Pressure

Effects of Preparation Parameters on Room Temperature Formation of Vanadium-Doped Tio2 Nanocrystalline Powder

Synthesis of Highly Dispersed Barium Titanate Nanoparticles by a Novel Solvothermal Method

Ba 4 Ti 13 O 30 Nanocrystals Prepared by Hydrothermal Method

Effect of NaOH Concentration on Formation of Ba4Ti13O30 and BaTi5O11 Nanocrystals Prepared by Hydrothermal Method

Composition and shape control of single-crystalline Ba1-xSrxTiO3 (x=0-1) nanocrystals via a solvothermal route

Formation Of Nanocrystalline Tin Film By Ion-Beam-Enhanced Deposition

BaTiO3 Nanocrystals: Hydrothermal Synthesis and Structural Characterization

Sol–gel based synthesis of ultrafine tetragonal BaTiO 3

Morphology and atomic-scale surface structure of barium titanate nanocrystals formed at hydrothermal conditions

Preparation for BaTiO3 Nano-crystalline Powder and Study on the Sintering Characteristics of Ceramic

Hydrothermal synthesis and morphology control mechanism of BaTiO3 from NaTi3O6(OH)(H2O)2 precursors

Preparation and Characterization of Monodispersed BaTiO3 Nanocrystals Using One-Step Solvothermal Method

Synthesis of BaTiO3 Nanowires at Low Temperature