Abstract:The microstructure of BaTiO3 (BT) nanocrystals was investigated by X-ray diffraction (XRD), scanning electron microscopy (SEM), selected area electron diffraction (SAED), and (high-resolution) transmission electron microscopy [(HR)TEM]. The BT nanocrystals have a cubic perovskite structure as revealed by XRD and SAED. They were prepared by a hydrothermal method using different starting materials: (i) Using as-prepared titanium hydroxide and barium hydroxide as starting materials, BT nanocrystals were obtained with a narrow size distribution and an average grain size of 65 nm, exhibiting a spherical particle morphology and smooth surfaces. These nanocrystals showed almost uniform contrast in TEM. HRTEM lattice fringe images indicate a rather uniform, perfect crystal structure. (ii) Using barium hydroxide and titanium dioxide (anatase) as starting materials, many coarse-faceted cubic nanocrystals and a small amount of spherical particle were observed, indicating a developed bimodal size distribution. Diffraction contrast variations across these particles indicate the presence of high strain in these BT particles. The strain is probably caused by the lattice defects like OH− ions and their compensation by cation vacancies. HRTEM images demonstrated that (1 0 0) and (1 1 0) surface facets are present on these particles. In addition they revealed the presence of very small-nucleated BT islands at the edges of the faceted particles.

Direct Synthesis of Ultrafine Tetragonal BaTiO3 Nanoparticles at Room Temperature

Room-Temperature Synthesis of BaTiO<sub>3</sub>Nanoparticles in Large Batches

Sol–gel based synthesis of ultrafine tetragonal BaTiO 3

Preparation of Nanoscaled BaTiO3 Powders by DSS Method Near Room Temperature under Normal Pressure

Room temperature synthesis of BaTiO3 nanoparticles using titanium bis(ammonium lactato) dihydroxide

Synthesis of Highly Dispersed Barium Titanate Nanoparticles by a Novel Solvothermal Method

Direct large-scale synthesis of perovskite barium strontium titanate nano-particles from solutions

Composition and shape control of single-crystalline Ba1-xSrxTiO3 (x=0-1) nanocrystals via a solvothermal route

Large-scale Synthesis of Nanocrystals of Barium Titanate and Other Titanates Through Solution-Phase Processes

Size-controlled synthesis of BaTiO3 nanocrystals via a hydrothermal route

Preparation of Single-Crystalline BaTi5O11 Nanocrystals by Hydrothermal Method

Formation mechanism of BaTiO3nanocrystalline synthesized at room temperature

Low-temperature synthesis of barium titanate thin films by nanoparticles electrophoretic deposition

Direct Synthesis of Barium Zirconate Titanate (BZT) Nanoparticles at Room Temperature and Sintering of Their Ceramics at Low Temperature

Morphology and atomic-scale surface structure of barium titanate nanocrystals formed at hydrothermal conditions

Low-temperature Synthesis of TiB2 Nanocrystals Using TiO2 ,LiBH4 and Mg

Synthesis and Characterization of BaTiO3 Nanopowders Via Solvothermal Method

Low-temperature Synthesis and Analysis of Barium Titanate Nanoparticles with Excess Barium

Ba 4 Ti 13 O 30 Nanocrystals Prepared by Hydrothermal Method

Stoichiometry of BaTiO 3 nanoparticles

BaTiO3 Nanocrystals: Hydrothermal Synthesis and Structural Characterization