Low Temperature Phase Transition Mechanism of Amorphous Al-oxalate to Nano Α-Alumina
Yaling Yu,Chenyang Zhang,Mingfeng Zhong,Huan Yang,Yunying Wu,Chanjin Liang,Chao Song,Wei Xu,Shaomin Lin,Zhijie Zhang
DOI: https://doi.org/10.1016/j.ceramint.2024.06.357
IF: 5.532
2024-01-01
Ceramics International
Abstract:alpha-Alumina (alpha-Al2O3), widely used as a raw material or production in advanced manufacturing industry, has attracted much attention in terms of its preparation temperature. A simple dissolution-evaporation-precipitation process was employed to obtain the amorphous Al-oxalate (AAO) precursor, serving as the starting material for the low temperature preparation of nano alpha-Al2O3. The crystalline structure and thermal behavior of the AAO were compared with commercially available aluminum hydroxide (Al(OH)(3)) powder using the X-ray powder diffraction (XRD) instrument, the thermal gravity analysis and differential scanning calorimetry (TG-DSC). The phase transition mechanism of AAO was investigated by the fourier transform infrared spectroscopy (FTIR), transmission electron microscope (TEM), scanning electron microscope (SEM), and Al-27 magic angle spinning nuclear magnetic resonance (Al-27-MAS-NMR). The DSC results indicated that AAO underwent a phase transformation at 982 degrees C. The alpha-alumina diffraction peaks appeared in AAO at 1000 degrees C, while alpha-Al2O3 phase was observed for Al(OH)(3) at 1200 degrees C. Furthermore, an absorption peak at 452 cm(-1), corresponding to Al-O bond in alpha-alumina was detected at 1000 degrees C. The proposed low-temperature preparation mechanism of alpha-alumina from AAO is as follows: four coordination Al-oxalate species entities coexist within the AAO sample; with increasing temperature, organic acid functional groups oxidize and volatilize, resulting in the formation of tetra-coordinate [AlO4], penta-coordinate [AlO5], and hexa-coordinate [AlO6] atomic groups; these atomic clusters further polymerize to form a structurally dense alpha-alumina crystal at the nano-scale (similar to 50 nm) at around 1000 degrees C. The experimental findings present a novel approach and method for the low-temperature preparation of nano-sized alumina powder. Additionally, a feasible theoretical reference for the low-temperature phase transition mechanism of amorphous Al-oxalate was provided.