Abstract:LaCoO3 thin films with perovskite structure were prepared on Si(lll) substrate successfully by using an amorphous heteronuclear complex, LaCo(DTPA). 6H(2)O (DTPA, diethylenetriaminepentaacetic acid), as a precursor. X-Ray diffraction (XRD) results indicated that the crystalline sizes of LaCoO3 films grew from 17.8 to 34.3 nm with the calcination temperature increasing from 550 to 800 degreesC for 1 h and the crystalline sizes of LaCoO3 films grew from 22.3 to 25.3 nm with the calcination time increasing from 1 to 6 h at 650 degreesC. Auger electron spectroscopy (AES) depth profile analysis indicated that the composition of the thin film was homogenous with depth the interface diffusion took place between LaCoO3 layer and Si substrate. The thickness of LaCoO3 thin film depended on the concentration of the precursor solution and could be described approximately by the following equation: d = 0.580c + 0.285c(2). Scanning electron microscopy (SEM) indicated that the texture of the film was governed by the concentration of precursor solution When the concentration of precursor solution was lower than 15%, a smooth film without microcrack was obtained. The texture of the film could be modified significantly by adding polyethylene glycol (PEG). But the thickness of the film was hardly influenced by the addition of PEG. (C) 2001 Elsevier Science B.V. All rights reserved.

Preparation Of Nanosized La1-Xsrxcoo3 Via La1-Xsrxco(Dtpa)Center Dot 6h(2)O Amorphous Complex Precursor

Preparation of nanosized La1−xSrxCoO3 via La1−xSrxCo(DTPA)·6H2O amorphous complex precursor

Preparation of nanosized LaCoO3 perovskite oxide using amorphous heteronuclear complex as a precursor at low temperature

Preparation of nanosized La2CuO4 perovskite oxide using an amorphous heteronuclear complex as a precursor at low-temperature

Preparation of nanosized LaCoxMn1−xO3 perovskite oxide using amorphous heteronuclear complex as a precursor

Preparation of nanosized perovskite LaNiO 3 powder via amorphous heteronuclear complex precursor

Crystal Structure Of La1-Xcexcoo3+Delta (X <= 0.1) Nanoparticles At Different Temperatures

Crystal Structure of La1−xCexCoO3+δ (x ≤0.1) nanoparticles at different temperatures

Low Temperature Synthesis of Nanosized La1-Xcaxmno3 Using Amorphous Molecular Alloys As Precursors

Preparation of Nanosized GdCoO 3 Powder Using Amorphous Heteronuclear Complex As a Precursor

Effect of La-Introduced Manner on the Phase Formation and Morphology of the Hydrothermally Synthesized Pb_(0.70)La_(0.30)TiO_3 Powders

Hydrothermally synthesized Pb0.70La0.30TiO3 powders

Synthesis of nanosized perovskite powder using amorphous complex method and their CO catalytic oxidation performance

Preparation of nano-sized SrAl2O4 using an amorphous hetero-nucleus complex as a precursor

Solid‐State Synthesis of LaCoO3 Perovskite Nanocrystals

Investigation of Precursors in the Preparation of Nanostructured La0.6Sr0.4Co0.2Fe0.8O3−δ Via a Modified Combined Complexing Method

A Novel Route to Synthesize Nano-Crystalline Ba0.5sr0.5co0.8fe0.2o3-Delta Perovskite Oxide at High Temperature

Influence Of Peg Additive And Precursor Concentration On The Preparation Of Lacoo3 Film With Perovskite Structure

From molecular alloys to nanoparticles of La0.67-xNdxSr0.33MnO3

Synthesis of Perovskite Structure (Ca-0.61, Nd-0.26)TiO3 Nanopaticles by Sol-Gel Method

PREPARATION OF NANOSIZED Bi3.25 La0.75 Ti3 O12 POWDER BY COPRECIPITATION METHOD