Molten Salt Route of La 1−x Ca X MnO 3 Nanoparticles: Microstructural Characterization, Magnetic and Electrical Transport Properties
Weiren Xia,Lei Li,Heng Wu,Piaojie Xue,Xinhua Zhu
DOI: https://doi.org/10.1016/j.matchar.2017.07.002
IF: 4.537
2017-01-01
Materials Characterization
Abstract:Single-crystalline La1−xCaxMnO3 (LCMO, x=0.3 and 0.5) nanoparticles synthesized by molten salt method, have been studied based on their microstructural characterization, magnetic and electrical transport property measurements. X-ray diffraction patterns and electron diffraction patterns reveal that all the LCMO nanoparticles crystallize in the orthorhombic perovskite structure (Pnma space group). TEM images show that the LCMO nanoparticles exhibit irregular shapes and their particle sizes are increased with increasing the annealed temperatures. The resolved (200) lattice fringes in high-resolution TEM images confirm the single crystalline nature of the LCMO nanoparticles. Magnetization measurements versus temperature show a paramagnetic – ferromagnetic transition for all the nanoparticles. Room temperature and low temperature M – H loops demonstrate that the LCMO nanoparticles exhibit ferromagnetic behavior at 5K, whereas a paramagnetic behavior at 300K. Resistivity behavior of the LCMO nanoparticles demonstrate that they exhibit a broad metal — insulator (M−I) transition, and the transition temperature shifts towards a high temperature under an external magnetic field. The magnetoresistance (MR) values of the LCMO nanoparticles were increased monotonically with decreasing the temperature below 300K, and finally reached constant values at temperatures below 100K. The MR value of the La0.5Ca0.5MnO3 nanoparticles annealed at 650°C for 3h, was found to be 77% at 50K in 5T, and 57% for the La0.7Ca0.3MnO3 nanoparticles annealed at 650°C for 3h. Such large MR values of the present LCMO nanoparticles make them ideal candidates for the spintronic devices.