Fabrication and characterization of Lal(1.8)Ca(0.2)MnO(3) nanowires

H Zhang,XY Ma,J Xu,DR Yang

2003-01-01

Abstract:La0. 8Ca0. 2MnO3 nanowires were prepared by using a simple sol-gel method with nano-channel alumina(NCA) as template. The effects of two kinds of annealing methods. on the structure, morphology of La0. 8Ca0. 2MnO3 nanowires were investigated. The diameter of La0. 8Ca0. 2MnO3 nanowires prepared by ramping the furnace temperature directly to 800 degreesC with a rate of 10 degreesC/min is larger than that of pores within NCA. While, the diameter of La0. 8Ca0. 2MnO3 nanowires prepared by ramping the furnace temperature to 400 degreesC with a rate of 2 degreesC /min and keeping at this temperature for I h, then ramping to 800 degreesC with a rate of 10 degreesC /min and keeping at this temperature for 2 h is nearly equivalent to that of pores within NCA. XRD and selected area electron diffraction indicate that the nanowires derived under the two annealing conditions are of monoclinic perovskite structure. It is demonstrated that the La0. 8Ca0. 2MnO3 nanowires with monoclinic perovskite structure can be fabricated at low temperatures by employing a solution route. The method presented in this paper is also feasible for fabricating the nanowires of other mono-component and multi-component oxides.