Generalized Synthesis of NaLn(MoO4)2 Nano/microcrystals (ln = La–Lu and Y): the Effects of Lanthanide Contraction, Structure, and Down-/Up-conversion Luminescence
Zhixin Xu,Siyuan Li,Qinghong Meng,Xuejiao Wang,Qi Zhu,Ji-Guang Li
DOI: https://doi.org/10.1016/j.jallcom.2020.154676
IF: 6.2
2020-01-01
Journal of Alloys and Compounds
Abstract:Systematic synthesis of scheelite-type double molybdate nano-/microcrystals NaLn (MoO4)(2) (Ln = La-Lu lanthanides and Y) was successfully carried out via hydrothermal reaction at 180 degrees C without using any organic additive, and the intrinsic effects of lanthanide contraction on phase preference and crystallite morphology were unambiguously observed. It was shown that the products of larger Ln(3+) (Ln = La-Dy) and smaller Ln(3+) (Ln = Ho-Lu and Y) elements crystallized as tetragonal NaLn (MoO4)(2) and new orthorhombic NaLnMo(2)O(8)center dot 2H(2)O structures, respectively, with the latter being able to dehydrate to tetragonal NaLn (MoO4)(2) upon calcination at similar to 300 degrees C. Y was found to be a demarcation point for the two structures, and phase preference was shown to be influenced by solution pH and MoO42-/Y3+ molar ratio. With Eu3+ as a downconversion (DC) luminescence probe, the effects of Ln type (Ln = La, Gd, Y and Lu) and crystal structure were manifested. Furthermore, the upconversion (UC) luminescence of Yb3+/Ho3+ and Yb3+/Er3+ pairs in NaLu(MoO4)(2) was studied for the first time, and strong red and green UC emissions were observed under the 978 nm laser excitation. Besides, the processes/mechanisms of UC were studied via varying the excitation power and were discussed with Yb3+-MoO42- dimer sensitizer. (c) 2020 Elsevier B.V. All rights reserved.