Abstract:Single-phase Li0.5-0.5xZnxFe2.5-0.5xO4 (where x=0.0, 0.2, 0.3, 0.4, 0.5 and 0.8) nanofibers with diameters of 50 similar to 100 nm were successfully fabricated via electrospinning technique in combination with subsequent heat treatment using polyvinylpyrrolidone, nickel nitrate, zinc nitrate and ferric nitrate as principal raw material. The thermal decomposition process of as-spun precursor nanofibers and the influences of the calcination temperature and chemical composition on the crystal structure, micromorphology and magnetic properties of the prepared nanofiber samples were investigated by means of thermogravimetric and differential thermal analysis, X-ray diffraction, field emission scanning electron microscopy, transmission electron microscopy and vibrating sample magnetometer. The results indicate that the pure crystalline LiZn ferrite nanofibers are basically formed when the precursor nanofibers are calcined at 350 degrees C for 2 h. As the calcination temperature increases from 350 to 600 degrees C, the average grain size of Li0.35Zn0.3Fe2.35O4 nanofibers ranges from 13.0 to 47.5 nm and the micromorphology evolves toward a chain-like structrue. The saturation magnetization of the samples monotonously increases from 39.7 to 84.5 A.m(2).kg(-1), while the coercivity increases initially, reaches a maximun value of 12.6 kA.m(-1) at 550 C and then decreases, which reveals that the magnetic single-domain critical size of Li0.35Zn0.3Fe2.35O4 nanofibers may be around 35 nm. The lattice constant of as-prepared Li0.5-0.5xZnxFe2.5-0.5xO4 nanofibers calcined at 500 degrees C for 2 h exhibits an almost linear increase with increasing x and complies with Vegard's law. The coercivity of these nanofiber samples gradually decreases from 17.1 kA.m(-1) for x=0.0 to 2.4 kA.m(-1) for x=0.8, and the saturation magnetization firstly increases to 74.7 A.m(2).kg(-1) with the value of x up to 0.3 and then decreases beyond this limit. Compared to the nanoparticle counterparts prepared under similar conditions, the LiZn ferrite nanofibers have a relatively high coercivity due to their large shape anisotropy. These LiZn ferrite nanofibers have potential application in many fields such as nanoelectronic devices, sensitive devices, microwave absorbers, and biomedicine.

Morphology dependence of electron spin resonance investigation on structure controllable hollow La0.7Sr0.3MnO3 nanofibres

Time-Resolved Optical Studies Of Spin And Quasiparticle Dynamics In Colossal Magnetoresistance Materials: La0.67ca0.33mno3, La0.67sr0.33mno3, And Sr2femoo6

Microstructure And Magnetic Anisotropy Of Electrospun Cu1-Xznxfe2o4 Nanofibres: A Local Probe Study

Tunable magnetization in nanoscale LuFeO3: Role of morphology, ortho-hexa phase ratio and local structure

Electrospun Magnetic SrFe12O19nanofibres with Improved Hard Magnetism

Ferromagnetic Fe3O4 Nanofibers: Electrospinning Synthesis and Characterization

Preparation and Peculiar Magnetic Properties at Low Temperatures of La1.85Sr0.15CuO4 Nanofibers

Preparation of nanosized La0.7Sr0.3MnO3/Pr0.5Sr0.5MnO3 composites with enhanced low-field magnetoresistance

Low-Field Magnetoresistance In Nanosized La0.7sr0.3mno3/Pr0.5sr0.5mno3 Composites

Enhanced Low Field Magnetoresistance in Nanocrystalline La0.7sr0.3mno3 Synthesized on Mgo Nanowires

Enhanced magnetoresistance in La0.7Sr0.3MnO3 nanoscaled granular composites

Enhanced magnetoresistance in La<sub>07</sub>Sr<sub>03</sub>MnO<sub>3</sub> nanoscaledgranular composites

Enhanced Magnetoresistance in La07Sr03MnO3 Nanoscaledgranular Composites

Electrospinning Preparation, Structural and Magnetic Properties of Li0.5-0.5xznxfe2.5-0.5xo4 Nanofibers

Synthesis of Ordered Ultra-Long Manganite Nanowires Via Electrospinning Method

Enhanced Magnetoresistance in La_(0.7)Sr_(0.3)MnO_3 Nanoscaled Granular Composites

Electron Spin Resonance Studies of (la0.6ln0.4)0.67ca0.33mno3 (ln = La, Pr, Nd and Sm) Nanoparticles at Different Temperatures

Enhanced Room Temperature Magnetoresistance in La0.7Sr0.3MnO3/Sm0.7Sr0.3MnO3 Nanocomposites

Determination Of Magnetic Parameters In La0.7sr0.3mno3/Srtio3 Thin Films Using Emcd

Low field magnetoresistance in La1-xSrxMnO 3-δ thin films: Effect of two-phase microstructure and oxygen deficiency

Spin-polarized inter-grain tunneling as the probable mechanism for low-field magnetoresistance in partially crystallized La0.5Sr0.5MnO3 thin films