Abstract:A large amount of CO as hazardous emission in the iron ore sintering process has caused severe harm to the environment and human health. To control the emission of CO more effectively, the preparation of highly efficient catalysts has attracted much attention. In this study, the La1-xSrxMnO3 (0 ≤ x < 1) perovskite catalysts with different Sr2+ contents were prepared by the one-step flame synthesis method to treat CO pollutants in the iron and steel industry. The influence of Sr2+ doping on the structure and activity of catalytic were characterized and analyzed. La1-xSrxMnO3 perovskite catalysts exhibit good perovskite phases and loose spherical structures. The specific surface areas are between 4.1 and 12.0 m2 g−1. Combined with the results of H2-TPR and O2-TPD, the improvement of catalytic activity of La1-xSrxMnO3 perovskite can be attributed to the high concentration of active centers and oxygen vacancies. Significantly, the La0.4Sr0.6MnO3 catalyst presented the best reducibility and high content of absorbed active oxygen species, leading to a superior CO oxidation catalytic activity and reaches 50% CO conversion at 134.9°C and 90% at 163.2°C, respectively. The effects of water vapor and CO2 on the oxidation activity of La1-xSrxMnO3 perovskite was investigated. The flame-produced catalysts exhibit favorable catalytic stability and antisintering ability, achieving 100% CO conversion after fifth consecutive oxidation cycles.

Preparation of nanosized LaCoxMn1−xO3 perovskite oxide using amorphous heteronuclear complex as a precursor

Preparation of nanosized LaCoO3 perovskite oxide using amorphous heteronuclear complex as a precursor at low temperature

Preparation of nanosized La2CuO4 perovskite oxide using an amorphous heteronuclear complex as a precursor at low-temperature

Preparation of nanosized La1−xSrxCoO3 via La1−xSrxCo(DTPA)·6H2O amorphous complex precursor

Preparation Of Nanosized La1-Xsrxcoo3 Via La1-Xsrxco(Dtpa)Center Dot 6h(2)O Amorphous Complex Precursor

Preparation of nanosized perovskite LaNiO 3 powder via amorphous heteronuclear complex precursor

Low Temperature Synthesis of Nanosized La1-Xcaxmno3 Using Amorphous Molecular Alloys As Precursors

Synthesis of nanosized perovskite powder using amorphous complex method and their CO catalytic oxidation performance

Dye degradation activity and stability of perovskite-type LaCoO 3-x (x = 0∼0.075)

Synthesis Of Nanostructure Lamno3 And Lacoo3 Catalysts And Their Catalytic Activity In Oxidation Reaction

Low Temperature Synthesis and Magnetism of La0.75Ca0.25MnO3 Nanoparticles

Structural Characterization and Co Oxidation Activity of Nanostructured Lamno3 Catalysts

From molecular alloys to nanoparticles of La0.67-xNdxSr0.33MnO3

Solid‐State Synthesis of LaCoO3 Perovskite Nanocrystals

Dye Degradation Activity and Stability of Perovskite-Type LaCoO<SUB>3&minus;<I>x</I></SUB> (&Lt;i>x</i>=0&sim;0.075)

Preparation of Nanosized GdCoO 3 Powder Using Amorphous Heteronuclear Complex As a Precursor

Preparation And Properties Of Ultra Fine Lamno3 And Lacoo3 Perovskite Compounds

LaFe1-xNixO3 perovskites in the catalytic reaction of high-temperature decomposition of nitrous oxide

Facile One-Step Flame Synthesis of La1−xSrxMnO3 Nanoparticles for CO Catalytic Oxidation

A novel method for the synthesis of perovskite-type mixed metal oxides by the inverse microemulsion technique

Preparation and characterization of the non-stoichiometric La–Mn perovskites