Abstract:In order to lower Cu-Cu bonding temperature and shorten bonding time applied for 3D integration, nanostructure has been introduced on bonding Cu surface. However, few studies have been reported on Nano Particles (NPs) formation by film deposition process such as pulsed laser deposition (PLD), which would be compatible with CMOS process. In this work Ag nanostructure containing strings of NPs was formed by optimized PLD process, which is mostly used for nanofilm deposition. Then NPs morphology was observed by scanning electron microscope (SEM) and transmission electron microscopy (TEM). Ag nanostructure was consisted of strings of loose mesh structures filled with NPs with size range from several milometers to tens of nanometcrs. They were compressible and of high movability, which was significantly benefit for lowering bonding temperature. With these Ag nanostructure on Cu pads, chips were pre-bonding at the low temperature of 180 degrees C for 5 min and afterwards all the chips were simultaneously annealed at the temperature of 200 degrees C for 25 min. After die shear test, average shear strength of 15.8 MPa was obtained and fracture surface was inspected by SEM. After TEM observation of bonding interface, continuous Cu-Ag-Cu interfaces with almost no void were observed. It confirmed low temperature Cu-Cu bonding with Ag nanostructure by PLD was a reliable and time-saving process, which might be a promising technology for 3D integration.

Low Temperature Fine-pitch Cu-Cu Bonding Using Au Nanoparticles As Intermediate

Low-Temperature Cu-Cu Bonding Using Silver Nanoparticles Fabricated by Physical Vapor Deposition

Low Temperature Cu-Cu Bonding Using Copper Nanoparticles Fabricated by High Pressure Pvd

Low Temperature Fine-Pitch Wafer-Level Cu-Cu Bonding Using Nanoparticles Fabricated by PVD

Low Temperature Cu-Cu Bonding Using Ag Nanoparticles By Pvd

Cu-Cu Bonding By Ag Nanostructure At Low Temperature Of 180 Degrees C

Low-Temperature Ultrasonic Bonding of Cu/Sn Microbumps with Au Layer for High Density Interconnection Applications

Cu-Cu bonding by Ag nanostructure at low temperature of 180 °C

Low Temperature Cu-Cu Bonding Using Ag Nanostructure for 3d Integration

Low Temperature and Low Pressure Cu-Cu Bonding with Ag Doped Cu Nanosolder Paste

Low temperature Cu bonding with large tolerance of surface oxidation

Characterization of low temperature bonding with Cu nanoparticles for electronic packaging application

Low temperature Au-Au bonding using Ag nanoparticles as intermediate for die attachment in power device packaging

Low-Temperature and Low-Pressure Cu–Cu Bonding by Highly Sinterable Cu Nanoparticle Paste

Low-temperature and Low-Pressure Cu-Cu Bonding by Pure Cu Nanosolder Paste for Wafer-Level Packaging

Low Temperature Cu-Cu Bonding Using an Intermediate Sacrificial Sn Layer

Preparation of PVP Coated Cu NPs and the Application for Low-Temperature Bonding

Design of Cu Nanoaggregates Composed of Ultra-Small Cu Nanoparticles for Cu-Cu Thermocompression Bonding

Sintering of Mixed CuAg Nanoparticles Pretreated by Formic Acid Vapor for CuCu Low Temperature Bonding

Low Temperature Bonding of Cu Metal through Sintering of AgNanoparticles for High Temperature Electronic Application

Thermal-stable Void-Free Interface Morphology and Bonding Mechanism of Low-Temperature Cu-Cu Bonding Using Ag Nanostructure As Intermediate