Abstract:In order to lower Cu-Cu bonding temperature and shorten bonding time applied for 3D integration, nanostructure has been introduced on bonding Cu surface. However, few studies have been reported on Nano Particles (NPs) formation by film deposition process such as pulsed laser deposition (PLD), which would be compatible with CMOS process. In this work Ag nanostructure containing strings of NPs was formed by optimized PLD process, which is mostly used for nanofilm deposition. Then NPs morphology was observed by scanning electron microscope (SEM) and transmission electron microscopy (TEM). Ag nanostructure was consisted of strings of loose mesh structures filled with NPs with size range from several milometers to tens of nanometcrs. They were compressible and of high movability, which was significantly benefit for lowering bonding temperature. With these Ag nanostructure on Cu pads, chips were pre-bonding at the low temperature of 180 degrees C for 5 min and afterwards all the chips were simultaneously annealed at the temperature of 200 degrees C for 25 min. After die shear test, average shear strength of 15.8 MPa was obtained and fracture surface was inspected by SEM. After TEM observation of bonding interface, continuous Cu-Ag-Cu interfaces with almost no void were observed. It confirmed low temperature Cu-Cu bonding with Ag nanostructure by PLD was a reliable and time-saving process, which might be a promising technology for 3D integration.

Characterization of low temperature bonding with Cu nanoparticles for electronic packaging application

Low Temperature Bonding Process Using Mixed Cu-Ag Nanoparticles for Electronic Packaging

Low Temperature Bonding of Cu Metal through Sintering of AgNanoparticles for High Temperature Electronic Application

Polymer-Protected Cu-Ag Mixed NPs for Low-Temperature Bonding Application

Rapid and Low Temperature Sintering Bonding Using Cu Nanoparticle Film for Power Electronic Packaging

Bonding of Cu to Cu bulks through the low temperature sintering of Ag nanoparticle paste

Low Temperature Cu-Cu Bonding Using Copper Nanoparticles Fabricated by High Pressure Pvd

Low Temperature Fine-pitch Cu-Cu Bonding Using Au Nanoparticles As Intermediate

Enhanced shear strength and microstructure of Cu–Cu interconnection by low-temperature sintering of Cu nanoparticles

Preparation of PVP Coated Cu NPs and the Application for Low-Temperature Bonding

Low Temperature Cu-Cu Bonding Using Ag Nanoparticles By Pvd

Low-Temperature Cu-Cu Bonding Using Silver Nanoparticles Fabricated by Physical Vapor Deposition

Preparation of Oxidation-Resistant Ag-Cu Alloy Nanoparticles by Polyol Method for Electronic Packaging

Low Temperature Sintering-Bonding Through In-Situ Formation of Ag Nanoparticles Using Micro-Scaled Ag_2O Composite Paste

Cu-Cu Bonding By Ag Nanostructure At Low Temperature Of 180 Degrees C

Sintering mechanisms and mechanical properties of joints bonded using silver nanoparticles for electronic packaging applications

Large-scale synthesis of Ag nanoparticles by polyol process for low temperature bonding application

Interfacial Bonding Mechanisms of Sintered Cu Nanoparticles on Different Metallization Surfaces

Low Temperature Cu-Cu Bonding Using Ag Nanostructure for 3d Integration

Interfacial Characterization of Low-Temperature Cu-to-Cu Direct Bonding with Chemical Mechanical Planarized Nanotwinned Cu Films