Abstract:We have developed a new sol-gel route to synthesise Al2O3-SiO2 composite aerogels with different alumina/silica (Al/Si) molar ratios using an inexpensive inorganic salt. The approach is straightforward, inexpensive, and it produces monolithic mesoporous material with high specific surface area heat-treated at elevated temperatures. The effects of different Al/Si molar ratios and calcination temperatures on the microstructures and properties of Al2O3-SiO2 composite aerogels are investigated in this study. Results show that SiO2 is essentially amorphous, while Al2O3 predominately exists as polycrystalline boehmite for the as-dried composite aerogels. With the increase of Al/Si molar ratios, the morphologies change from connected spheroidal particles to nanometer-sized fibrous particles and web-like microstructures with varying diameters. As the heat treatment temperature increases to 600 degrees C, structural transition from boehmite to gamma-Al2O3 occurs within all the composite aerogels, and mullitization firstly occurs with the Al/Si molar ratio of 1 at around 1000 degrees C. The specific surface area undergoes an increase-decrease-increase process at 600 degrees C and 1200 degrees C for the composite aerogels with different Al/Si molar ratios. The specific surface area is as high as 166 m(2) g(-1) at 1200 degrees C for the sample with an Al/Si molar ratio of 8, which is higher than ever reported. The thermal conductivities of mullite fiber mat reinforced aerogel composites at room temperatures are 0.023 W m(-1) K-1, 0.029 W m(-1) K-1 and 0.025 W m(-1) K-1 with the Al/Si molar ratios of 2, 3 and 8, respectively, suitable for efficient thermal insulations uses.

Preparation and Characterization of ZrO2-Al2O3 Composite Aerogels

Synthesis and characterization of SiO2-Al2O3 composite aerogel using inorganic aluminum salt as raw material

Preparation and Characterization of Alumina-coated Hollow Quartz Fiber Reinforced Al2O3-SiO2 Aerogel Composite

Characterization of High-Surface-Area Zirconia Aerogel Synthesized from Combined Alcohothermal and Supercritical Fluid Drying Techniques

Preparation and Heat Treatment of Titania Aerogels by Ambient Pressure Drying

Highly thermally stable zirconia/silica composite aerogels prepared by supercritical deposition

Preparation and Characterization of C/Al 2 O 3 Composite Aerogel with High Compressive Strength and Low Thermal Conductivity

Preparation and Characterization of High Surface Area Zro2 Aerogel Modified by Sio2

Facile preparation of ZrCO composite aerogel with high specific surface area and low thermal conductivity

Fabrication and Thermal Stability of La2O3 Doped Alumina Aerogel

Preparation of Alumina Aerogel via Supercritical Method

One-step Synthesis of Monolithic Micro-Nano Yttria Stabilized ZrO2-Al2O3 Composite Aerogel

ZrC/C aerogel with high compressive strength by a carbothermic process

Preparation and Characterization of Hydrophobic Mesoporous SiO2 Aerogel

Preparation of SiO2-ZrO2 Aerogels and the Adsorption Performance for Cerium

Novel Al2O3–SiO2 composite aerogels with high specific surface area at elevated temperatures with different alumina/silica molar ratios prepared by a non-alkoxide sol–gel method

Preparation and properties of the Al2O3–SiO2 aerogel/alumina framework composite

Preparation of La2Zr2O7 composite SiO2 aerogels and their fiber-reinforced materials for thermal insulation applications

A Facile Method to Fabricate Al2O3-SiO2 Aerogels with Low Shrinkage up to 1200 °C

Synthesis of high-temperature resistant monolithic zirconia-based aerogel via facile water glass assisted sol–gel method

Synthesis of High-Surface-Area Alumina Aerogels without the Use of Alkoxide Precursors