Abstract:Silica aerogel has been formed using CO2 gas as the gelation agent through the low-cost ambient pressure drying technique. With water wash and the following solvent exchange process for Na+ removal, this synthesis route has no ion exchange resin used and becomes more straightforward. In order to reduce the silica particle and pore sizes, different hydrolysis-condensation rate control agents including dimethylformamide (DMF), methyl-triethoxysilane (TMES), Glycerol and methyltrimethoxylsilane (MTMS) have been applied to modify the structural groups of silica network. Results show that MTMS is the most effective control agent and the optimized MTMS/silica sol volume ratio has been found at 1% by testing the specific surface area of the aerogel. In addition, the effects of chlorotrimethylsilane (TMCS) amount and the calcining temperature on the physicochemical properties of the aerogel have been also investigated. When the TMCS/silica sol volume ratio is 0.4, Thermogravimetric and Differential Scanning Calorimetry analysis (TG/DSC) measurement shows that there is an apprent exothermic peak at calcining temperture of 420 degrees C, caused by the transformation of Si-CH3 group to Si-OH group. X-ray photoelectric spectroscopy (XPS) results show that the percentages of Si-C(-H) bonds with binding energy of 102.4 eV have decreased from 25.5% to 7.2% after 420 degrees C calcining. The contact angle of the as-dried aerogel is as high as 154 and dramatically decreases to ca. 109 degrees after calcining at 450 degrees C. The pore volume and BET specific surface area both increase first and then decrease with the increase of calcining temperature, and the pore volume reaches the maxmium of 1.45 cm(3)/g at 400 degrees C and it confirms Si-CH3 group release. This study offers a new facile route to the synthesis of silica aerogel and presents a promising way of the cost-effective large-scale manufacturing.

Preparation and Characterization of High Surface Area Zro2 Aerogel Modified by Sio2

Preparation and Heat Treatment of Titania Aerogels by Ambient Pressure Drying

Characterization of High-Surface-Area Zirconia Aerogel Synthesized from Combined Alcohothermal and Supercritical Fluid Drying Techniques

Preparation of monolithic titania aerogels with high surface area by a sol–gel process combined surface modification

Preparation and Characterization of Hydrophobic Silica Aerogel by Ambient Pressure Drying Method

Preparation and Characterization of Hydrophobic Mesoporous SiO2 Aerogel

Synthesis of high-temperature resistant monolithic zirconia-based aerogel via facile water glass assisted sol–gel method

Low-density, high-strength and large-scaled monolithic carbon aerogels fabricated via modified ambient pressure drying

ZrC/C aerogel with high compressive strength by a carbothermic process

Facile preparation of ZrCO composite aerogel with high specific surface area and low thermal conductivity

Synthesis of high specific surface area silica aerogel from rice husk ash via ambient pressure drying

Preparation of Methyltrimethoxysilane Derived Silica Aerogel Films via Ambient Pressure Drying

Synthesis and characterization of SiO2-Al2O3 composite aerogel using inorganic aluminum salt as raw material

Synthesis and characterization of silica aerogels by a novel fast ambient pressure drying process

Preparation of SiO2-ZrO2 Aerogels and the Adsorption Performance for Cerium

Synthesis of ZrO2 aerogels by supercritical CO2 fluid drying technology

Study on Silica Aerogel Modified by Trimethylchlorosilane

A Novel Na2O-B2O3-SiO2 System Aerogel

Synthesis and Textural Evolution of Mesoporous Si3N4 Aerogel with High Specific Surface Area and Excellent Thermal Insulation Property Via the Urea Assisted Sol-Gel Technique

Silica aerogels formed from soluble silicates and methyl trimethoxysilane (MTMS) using CO2 gas as a gelation agent

Preparation of high-strength silica aerogels by two-step surface modification via ambient pressure drying