Abstract:Highly porous and hydrophobic silica aerogel is fabricated using fly ash and trona ore as the starting materials and the cost-effective ambient pressure drying technique. The optimal calcination parameters are determined as temperature of 850°C, holding time of 2h, and the trona ore/fly ash mass ratio of 1.4. The CO2 release mechanism during calcination is proposed and has been verified by the Thermogravimetric and Differential Scanning Calorimetry analysis (TG/DSC) and X-ray fluorescence (XRF) technique. The hydrogel is derived from reacting the calcination mixture with sulphuric acid solution, followed by filtration. The impurities can be effectively removed through water washing and solvent exchange processes. No ion exchange resin is used in this preparation method, and thus it is a safe, inexpensive and much more straightforward process. In order to minimize drying shrinkage, the hydrogel is first transformed into an alcogel by soaking in ethanol, after which the alcogel is surface modified with the hexane/ethanol/trimethylchlorosilane (hexane/ethanol/TMCS) mixture solution. It has been observed that the specific surface area, BJH desorption pore volume, and BJH desorption average pore diameter all first increase and then decrease so that reach to the maximum values once the heat treatment temperature approaches 500°C due to the oxidation of CH3 groups on the silica skeleton surface. The final product presents special characteristics including: (1) high thermal stability for maintaining hydrophobicity up to 476°C, (2) contact angle of the as-dried silica aerogel as high as 151°, (3) silica particle size of ca. 3–6nm, agreeing well with the model as reported, (4) and the 500°C heat treated sample possessing a large specific surface area of 856.2m2/g, a large pore volume of 2.92cm3/g, and a BJH desorption average pore diameter of 17.1nm. The proposed inexpensive approach produces silica aerogel with superior properties and is a scalable-manufacturing method for large-scale industrial production.

Characterization of High-Surface-Area Zirconia Aerogel Synthesized from Combined Alcohothermal and Supercritical Fluid Drying Techniques

A Simple Alcohothermal Synthetic Route to High Surface Area Zirconia Aerogel

Highly thermally stable zirconia/silica composite aerogels prepared by supercritical deposition

A Novel Preparation Process for Thermally Stable Ultrafine Tetragonal Zirconia Aerogel

Synthesis of ZrO2 aerogels by supercritical CO2 fluid drying technology

Preparation and Characterization of High Surface Area Zro2 Aerogel Modified by Sio2

Synthesis of high-temperature resistant monolithic zirconia-based aerogel via facile water glass assisted sol–gel method

Synthesis of a novel Al 2 O 3 –SiO 2 composite aerogel with high specific surface area at elevated temperatures using inexpensive inorganic salt of aluminum

A novel low-cost method of silica aerogel fabrication using fly ash and trona ore with ambient pressure drying technique

Postsynthetic modification of yttria‐stabilized zirconia aerogels with silica coatings for enhanced thermal stability

Synthesis of High-Surface-Area Alumina Aerogels without the Use of Alkoxide Precursors

Synthesis and characterization of SiO2-Al2O3 composite aerogel using inorganic aluminum salt as raw material

Preparation and Characterization of C/Al 2 O 3 Composite Aerogel with High Compressive Strength and Low Thermal Conductivity

One-step Synthesis of Monolithic Micro-Nano Yttria Stabilized ZrO2-Al2O3 Composite Aerogel

Synthesis of Alumina Aerogels by Ambient Drying Method and Control of Their Structures

Preparation and Characterization of Hydrophobic Mesoporous SiO2 Aerogel

Preparation and Characterization of Alumina-coated Hollow Quartz Fiber Reinforced Al2O3-SiO2 Aerogel Composite

Design and preparation of novel Y2O3-SiO2 composite aerogels for high-temperature thermal insulators

In-situ acid catalysis strategy to achieve rapid ambient pressure drying preparation of aerogels

Facile preparation of ZrCO composite aerogel with high specific surface area and low thermal conductivity

Synthesis of alumina aerogel enriched carboxymethyl cellulose with polymodal pore size distribution by ambient pressure drying