Abstract:We have developed a new sol-gel route to synthesise Al2O3-SiO2 composite aerogels with different alumina/silica (Al/Si) molar ratios using an inexpensive inorganic salt. The approach is straightforward, inexpensive, and it produces monolithic mesoporous material with high specific surface area heat-treated at elevated temperatures. The effects of different Al/Si molar ratios and calcination temperatures on the microstructures and properties of Al2O3-SiO2 composite aerogels are investigated in this study. Results show that SiO2 is essentially amorphous, while Al2O3 predominately exists as polycrystalline boehmite for the as-dried composite aerogels. With the increase of Al/Si molar ratios, the morphologies change from connected spheroidal particles to nanometer-sized fibrous particles and web-like microstructures with varying diameters. As the heat treatment temperature increases to 600 degrees C, structural transition from boehmite to gamma-Al2O3 occurs within all the composite aerogels, and mullitization firstly occurs with the Al/Si molar ratio of 1 at around 1000 degrees C. The specific surface area undergoes an increase-decrease-increase process at 600 degrees C and 1200 degrees C for the composite aerogels with different Al/Si molar ratios. The specific surface area is as high as 166 m(2) g(-1) at 1200 degrees C for the sample with an Al/Si molar ratio of 8, which is higher than ever reported. The thermal conductivities of mullite fiber mat reinforced aerogel composites at room temperatures are 0.023 W m(-1) K-1, 0.029 W m(-1) K-1 and 0.025 W m(-1) K-1 with the Al/Si molar ratios of 2, 3 and 8, respectively, suitable for efficient thermal insulations uses.

Preparation and Characterization of C/Al 2 O 3 Composite Aerogel with High Compressive Strength and Low Thermal Conductivity

Carbon-Fiber Felt Reinforced Carbon/Alumina Aerogel Composite Fabricated with High Strength and Low Thermal Conductivity

Preparation of the Novel B4C–SiC Composite Aerogel with High Compressive Strength and Low Thermal Conductivity

Fabrication of Al2O3 aerogel-SiO2 fiber composite with enhanced thermal insulation and high heat resistance

Fabrication of the SiC/HfC Composite Aerogel with Ultra-Low Thermal Conductivity and Excellent Compressive Strength

Preparation and Characterization of Alumina-coated Hollow Quartz Fiber Reinforced Al2O3-SiO2 Aerogel Composite

ZrC/C aerogel with high compressive strength by a carbothermic process

Synthesis and characterization of SiO2-Al2O3 composite aerogel using inorganic aluminum salt as raw material

Robust monolithic polymer(resorcinol-formaldehyde) reinforced alumina aerogel composites with mutually interpenetrating networks

Preparation of Alumina Aerogel via Supercritical Method

Synthesis of alumina aerogel enriched carboxymethyl cellulose with polymodal pore size distribution by ambient pressure drying

Facile preparation of ZrCO composite aerogel with high specific surface area and low thermal conductivity

Fiber-Reinforced Coal Gangue-Based Alumina Aerogel Composites with Highly Thermal Stability by Ambient Pressure Drying

Novel Al2O3–SiO2 composite aerogels with high specific surface area at elevated temperatures with different alumina/silica molar ratios prepared by a non-alkoxide sol–gel method

Rapid preparation of Palygorskite/Al2O3 composite aerogels with superhydrophobicity, high-temperature thermal insulation and improved mechanical properties

Novel silica-modified boehmite aerogels and fiber-reinforced insulation composites with ultra-high thermal stability and low thermal conductivity

Facile synthesis of mullite fiber/alumina composite aerogel with enhanced bending strength and controllable thermal insulation performance

A Facile Method to Fabricate Al2O3-SiO2 Aerogels with Low Shrinkage up to 1200 °C

Fabrication of SiCN(O) Aerogel Composites with Low Thermal Conductivity by Wrapping Mesoporous Aerogel Structures over Mullite Fibers

Preparation and properties of the Al2O3–SiO2 aerogel/alumina framework composite

Synthesis of Al2O3-SiO2 aerogels with low thermal conductivity and high strength by methyltriethoxysilane as a silica precursor